Aremco Aremco-Bond™ 2200 High Performance Epoxide
| Category | Polymer , Adhesive , Thermoset , Epoxy |
| Manufacturer | Aremco |
| Trade Name | Aremco-Bond™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aremco Aremco-Bond™ 2200 High Performance Epoxide.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Glass Fiber- and Kevlar-Reinforced, Epoxy-Novolac; High Strength, Excellent Abrasion and Corrosion Resistance
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.60 g/cc | 1.60 g/cc |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 88 | 88 | |
| Flexural Strength | 92.4 MPa | 13400 psi | ASTM D790 |
| Shear Strength | 16.5 MPa | 2400 psi | ASTM D1002-94 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 34.2 µm/m-°C @Temperature 20.0 °C |
19.0 µin/in-°F @Temperature 68.0 °F |
|
| Maximum Service Temperature, Air | 204 °C | 400 °F | |
| Minimum Service Temperature, Air | -55.0 °C | -67.0 °F | |
| Shrinkage | 0.90 % | 0.90 % | Cure Shrinkage |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | |
| Dielectric Constant | 4.7 @Frequency 1000 Hz |
4.7 @Frequency 1000 Hz |
|
| Dielectric Strength | 18.1 kV/mm | 460 kV/in | |
| Dissipation Factor | 0.010 | 0.010 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 240 min @Temperature 175 °C |
4.00 hour @Temperature 347 °F |
Alternate Cure |
| 1440 - 2880 min @Temperature 23.0 °C |
24.0 - 48.0 hour @Temperature 73.4 °F |
Recommended Cure | |
| Pot Life | 42.0 min @Temperature 25.0 °C |
42.0 min @Temperature 77.0 °F |
100 gm mass |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Chemical Resistance | Good | |
| Color | Rust Brown | |
| Mix Ratio By Weight | 1:1 | resin:hardener |
| Viscosity | Paste |
Users viewing this material also viewed the following:
- PEAK Werkstoff DISPAL S263 Aluminum Alloy, AlSi25Cu3Fe3Ni3MgCoTi, Condition T4
- PolyOne Lubri-Tech™ PF-30CF/15T Polysulfone, Carbon Fiber Reinforced, PTFE Lubricated (discontinued **)
- Kraton® D4153 E (O/E SBS) Linear Block Copolymer
- SABIC Innovative Plastics NORYL WCD795 PPE-TPE (Asia Pacific)
- Hexcel® HexWeb® CR-PAA™ 1/4-5056-0.0025 Phosphoric Acid Anodized Aluminum Honeycomb
- 3M 31U23CUV (Clear) Polyethylene Protective UV Tape
- 3M Scotchcal™ ElectroCut™ 7125-357 Graphic Film
- Gouda Vuurvast FI 25-12 Insulating Refractory Brick
- Hexion Bakelite™ PF 8052 Phenolic Formaldehyde Resin, Resistant to High Temperatures (discontinued **)
Copyright © lookpolymers.com All Rights Reserved