ArcelorMittal FB 540 Hot rolled ferrite-bainite steel

Category	Metal , Ferrous Metal , Alloy Steel
Manufacturer	ArcelorMittal
Trade Name	FB
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	ArcelorMittal FB 540 Hot rolled ferrite-bainite steel.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Description: This range of hot-rolled high strength steels has been developed to meet weight reduction requirements. It comprises four strength levels: FB 450, 540, 560 and 590. This family of steels extends the HSLA range of micro-alloyed steels to include products combining high tensile strength (UTS) with excellent formability and hole expansion (stretch flangeability) based on their ferrite-bainite microstructure.Applications: These steels are cold-drawn. The main applications are:structural parts (longitudinal beams, cross beams, car-body and ground liason parts),wheels,mechanical parts (ground liason parts, gear boxes...).ArcelorMittal has an extensive database relating to the forming and service properties of the entire range of ferrite-bainite steels. To integrate these steels at the design stage, a team of experts is available to perform specific studies based on modeling or laboratory tests.Information provided by ArcelorMittal

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	540 - 610 MPa	78300 - 88500 psi
Tensile Strength, Yield	400 - 485 MPa	58000 - 70300 psi
Elongation at Break	>= 18 %	>= 18 %	L<Sub>0</sub>=80 mm, th<3 mm
	>= 25 %	>= 25 %	L<Sub>0</sub>=5.65v <Sub>0</sub> mm, th<3 mm
Fatigue Strength	<= 405 MPa @# of Cycles 2.00e+6	<= 58700 psi @# of Cycles 2.00e+6
	<= 405 MPa @# of Cycles 1.00e+7	<= 58700 psi @# of Cycles 1.00e+7
	<= 480 MPa @# of Cycles 100000	<= 69600 psi @# of Cycles 100000

Component Elements Properties	Metric	English	Comments
Carbon, C	<= 0.17 %	<= 0.17 %
Iron, Fe	>= 98.18 %	>= 98.18 %	as balance
Manganese, Mn	<= 1.5 %	<= 1.5 %
Silicon, Si	<= 0.15 %	<= 0.15 %