Aptek 6108-PMF Epoxy Coating/Encapsulant

Category	Polymer , Thermoset , Epoxy , Epoxy Encapsulant, Unreinforced
Manufacturer	Aptek Laboratories
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Aptek 6108-PMF Epoxy Coating/Encapsulant.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

High temperature, rigid, electrical/electronic coating or encapsulant. Provides excellent environmental protection for continuous exposure to 220°C.Information provided by Aptek Laboratories, Inc.

Physical Properties	Metric	English	Comments
Density	1.20 g/cc	0.0434 lb/in³	ASTM D1475
Viscosity	2400 cP	2400 cP	Spindle #2; speed 10 rpm; ASTM D1824
Outgassing - Total Mass Loss	0.10 %	0.10 %	Cured property; at 10E-6 torr; ASTM E595
Collected Volatile Condensable Material	0.010 %	0.010 %	Cured property; at 10E-6 torr; ASTM E595

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	88	88	Cured property; ASTM D2240

Thermal Properties	Metric	English	Comments
CTE, linear	72.0 µm/m-°C @Temperature 20.0 °C	40.0 µin/in-°F @Temperature 68.0 °F	Cured property; alpha 1; Perkin Elmer TMS-2
	200 µm/m-°C @Temperature 20.0 °C	111 µin/in-°F @Temperature 68.0 °F	Cured property; alpha 2; Perkin Elmer TMS-2
Maximum Service Temperature, Air	220 °C	428 °F	Continuous
Glass Transition Temp, Tg	165 °C	329 °F	Cured property; Perkin Elmer TMS-2
Flash Point	200 °C	392 °F	ASTM D92

Electrical Properties	Metric	English	Comments
Volume Resistivity	>= 1.00e+15 ohm-cm	>= 1.00e+15 ohm-cm	Cured property; ASTM D257
Dielectric Constant	3.3 @Frequency 1000 Hz	3.3 @Frequency 1000 Hz	Cured property; ASTM D150
Dissipation Factor	0.0090 @Frequency 1000 Hz	0.0090 @Frequency 1000 Hz	Cured property; ASTM D150

Processing Properties	Metric	English	Comments
Processing Temperature	170 °C	338 °F	Gel 1 hr at 100°C to demold parts; Post Cure for 8 hours at 170°C

Descriptive Properties	Value	Comments
Color	Clear Amber