Amity Thermosets ATM 123 Phenolic Molding Organic Filler, Compression Molded

Category Polymer , Thermoset , Filled/Reinforced Thermoset , Phenolic
Manufacturer Amity Thermosets
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Amity Thermosets ATM 123 Phenolic Molding Organic Filler, Compression Molded.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Characteristics:Glossy surface free of filler marks Surface good & free of flaws Good mouldabilitySurface free of filler marks even after turningGood mechanical strengthColor-black, brownMedium flowApplications: Textile drums, bobbins & other textile machine parts Bottle caps ( big size )Glossy knobsComponents which ought to be polished after moulding , etc.Information provided by Amity Thermosets Limited
Physical Properties Metric English Comments
Density 1.32 - 1.38 g/cc
0.0477 - 0.0499 lb/in³
Molding; IS 867-1963
Apparent Bulk Density 0.680 - 0.720 g/cc
0.0246 - 0.0260 lb/in³
IS 867-1963
Water Absorption 0.26 - 0.39 %
0.26 - 0.39 %
IS 13411-1993
Linear Mold Shrinkage 0.0081 - 0.0089 cm/cm
0.0081 - 0.0089 in/in
IS 13411-1992
Mechanical Properties Metric English Comments
Tensile Strength at Break >= 46.0 MPa
>= 6670 psi
5 mm/min.; IS 867-1963
Shear Strength >= 60.0 MPa
>= 8700 psi
IS 867-1963
Izod Impact, Notched >= 0.220 J/cm
>= 0.412 ft-lb/in
IS 13411-1992
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+11 ohm-cm
>= 1.00e+11 ohm-cm
IS 3396-1979
Surface Resistance >= 1.00e+10 ohm
>= 1.00e+10 ohm
IS 3396-1979
Dielectric Strength >= 4.00 kV/mm

@Temperature 90.0 °C
>= 102 kV/in

@Temperature 194 °F
IS 2584-1963
Processing Properties Metric English Comments
Mold Temperature 160 - 180 °C
320 - 356 °F
Moisture Content 2.2 - 4.5 %
2.2 - 4.5 %
Injection Pressure 15.68 - 34.3 MPa
2274 - 4970 psi
Mold Pressure
Cure Time 0.333 - 0.417 min
0.00556 - 0.00694 hour
per mm
Shelf Life 12.0 Month
12.0 Month