Amity Thermosets ATI 102 Phenolic Molding Organic Filler, Injection Molded

Category Polymer , Thermoset , Filled/Reinforced Thermoset , Phenolic
Manufacturer Amity Thermosets
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Amity Thermosets ATI 102 Phenolic Molding Organic Filler, Injection Molded.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Characteristics:Electrical low loss Good mechanical strengthHigh electrical insulationGood mechanical strengthGlossy surfaceLow water absorptionColor-blackVery soft flow Applications: Electric switchgear components ( eg. relays ) Telecommunication equipment partsElectronic equipment partsAutomotive ( electronic and electrical ) parts Medium tension pulleysHigh gloss toilet seatsBig meter coversCircuit breaking switchesCoffee machine basesAutomobile light and signaling switches Moulding which ought to have overall good propertiesSolenoid switch covers, knobs and tops (superior quality), etc. Information provided by Amity Thermosets Limited
Physical Properties Metric English Comments
Density 1.32 - 1.38 g/cc
0.0477 - 0.0499 lb/in³
Molding; IS 867-1963
Apparent Bulk Density 0.600 - 0.660 g/cc
0.0217 - 0.0238 lb/in³
IS 867-1963
Water Absorption 0.20 - 0.40 %
0.20 - 0.40 %
IS 13411-1993
Linear Mold Shrinkage 0.0070 - 0.010 cm/cm
0.0070 - 0.010 in/in
IS 13411-1992
Mechanical Properties Metric English Comments
Tensile Strength at Break 46.0 - 53.0 MPa
6670 - 7690 psi
5 mm/min.; IS 867-1963
Shear Strength 67.0 - 77.0 MPa
9720 - 11200 psi
IS 867-1963
Izod Impact, Notched 0.220 - 0.300 J/cm
0.412 - 0.562 ft-lb/in
IS 13411-1992
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+11 - 1.00e+12 ohm-cm
1.00e+11 - 1.00e+12 ohm-cm
IS 3396-1979
Surface Resistance 3.2e+10 - 3.2e+11 ohm
3.2e+10 - 3.2e+11 ohm
IS 3396-1979
Dielectric Strength 6.00 - 8.00 kV/mm

@Temperature 90.0 °C
152 - 203 kV/in

@Temperature 194 °F
IS 2584-1963
Comparative Tracking Index >= 135 V
>= 135 V
2824-1975
Processing Properties Metric English Comments
Rear Barrel Temperature 65.0 - 85.0 °C
149 - 185 °F
Front Barrel Temperature 85.0 - 95.0 °C
185 - 203 °F
Nozzle Temperature <= 105 °C
<= 221 °F
Mold Temperature 160 - 180 °C
320 - 356 °F
Injection Pressure 98.0 - 196 MPa
14200 - 28400 psi
Hold Pressure 58.8 MPa
8530 psi
Cure Time 0.200 - 0.333 min
0.00333 - 0.00556 hour
per mm
Shelf Life 12.0 Month
12.0 Month
10-25°C