Americas Styrenics Styron® 8100 MFD High Impact Polystyrene  (discontinued **)

Category Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Impact Modified
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Americas Styrenics Styron® 8100 MFD High Impact Polystyrene  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
STYRON 8100 MFD high impact polystyrene is designed for microfloppy diskettes (MFD) applications. It offers easy processing, coloring, abrasion resistance, impact strength, and high heat resistance. When used unmodified for the manufacture of food contact articles STYRON 8100 MFD complies with the US Food, Drug and Cosmetic Act and Food Additive Regulations 21 CFR 177.1640. The regulations should be consulted for complete details.Data provided by Dow Chemical.Americas Styrenics was formed in 2008 as a joint venture between Dow Chemical and Chevron Phillips Chemical Company. Styron was a Dow trade name before the JV formation.
Physical Properties Metric English Comments
Density 1.04 g/cc
0.0376 lb/in³
ASTM Data
Linear Mold Shrinkage 0.0050 cm/cm
0.0050 in/in
Melt Flow 3.6 g/10 min

@Load 5.00 kg,
Temperature 200 °C
3.6 g/10 min

@Load 11.0 lb,
Temperature 392 °F
ASTM Data
Mechanical Properties Metric English Comments
Hardness, Rockwell R 105
105
Tensile Strength, Ultimate 25.0 MPa
3630 psi
ASTM Data
Tensile Strength, Yield 27.0 MPa
3920 psi
ASTM Data
Elongation at Break 51 %
51 %
ASTM Data
Tensile Modulus 2.17 GPa
315 ksi
ASTM Data
Izod Impact, Notched 1.12 J/cm
2.10 ft-lb/in
ASTM Data
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 78.0 µm/m-°C

@Temperature 20.0 °C
43.3 µin/in-°F

@Temperature 68.0 °F
ASTM data
Deflection Temperature at 0.46 MPa (66 psi) 93.0 °C
199 °F
Unannealed; ASTM Data
Deflection Temperature at 1.8 MPa (264 psi) 77.0 °C
171 °F
Unannealed; ASTM Data
Vicat Softening Point 104 °C
219 °F
Flammability, UL94 HB

@Thickness 3.10 mm
HB

@Thickness 0.122 in