Americas Styrenics Styron® 6010 High Impact Polystyrene  (discontinued **)

Category Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Flame Retardant
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Americas Styrenics Styron® 6010 High Impact Polystyrene  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
STYRON® 6010 resin is a high impact polystyrene grade with a proprietary ignition resistance additive package to achieve a UL 94 V-0 rating. It offers high heat resistance, high modulus, good impact strength and processability.Data provided by Dow Chemical.Americas Styrenics was formed in 2008 as a joint venture between Dow Chemical and Chevron Phillips Chemical Company. Styron was a Dow trade name before the JV formation.
Physical Properties Metric English Comments
Density 1.17 g/cc
0.0423 lb/in³
ASTM Data
Melt Density 1.09 g/cc
0.0394 lb/in³
Melt density
Linear Mold Shrinkage 0.0045 cm/cm
0.0045 in/in
Melt Flow 10.4 g/10 min

@Load 5.00 kg,
Temperature 200 °C
10.4 g/10 min

@Load 11.0 lb,
Temperature 392 °F
ASTM Data
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 23.0 MPa
3340 psi
ASTM Data
Tensile Strength, Yield 27.0 MPa
3920 psi
ASTM Data
Elongation at Break 48 %
48 %
ASTM Data
Elongation at Yield 1.7 %
1.7 %
ISO Data
Tensile Modulus 1.97 GPa
286 ksi
ASTM Data
Izod Impact, Notched 1.28 J/cm
2.40 ft-lb/in
ASTM Data
Charpy Impact Unnotched 5.00 J/cm²
23.8 ft-lb/in²
ISO Data, Low Temp
6.00 J/cm²
28.6 ft-lb/in²
ISO Data
Charpy Impact, Notched 0.200 J/cm²
0.952 ft-lb/in²
ISO Data, Low Temp
1.00 J/cm²
4.76 ft-lb/in²
ISO Data
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 85.0 µm/m-°C

@Temperature 20.0 °C
47.2 µin/in-°F

@Temperature 68.0 °F
ISO data
Specific Heat Capacity 1.90 J/g-°C
0.454 BTU/lb-°F
Thermal Conductivity 0.168 W/m-K
1.17 BTU-in/hr-ft²-°F
Deflection Temperature at 0.46 MPa (66 psi) 78.0 °C
172 °F
Unannealed; ASTM Data
Deflection Temperature at 1.8 MPa (264 psi) 68.0 °C
154 °F
Unannealed; ASTM Data
Vicat Softening Point 92.0 °C
198 °F
Flammability, UL94 V-0

@Thickness 2.00 mm
V-0

@Thickness 0.0787 in