AlphaGary Evoprene™ LF 6154 Automotive Thermoplastic Elastomer

Category Polymer , Thermoplastic , Elastomer, TPE , Styrenic TPE
Manufacturer AlphaGary
Trade Name Evoprene™ LF
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF AlphaGary Evoprene™ LF 6154 Automotive Thermoplastic Elastomer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Evoprene™ LF is a hydrogenated styrene block copolymer based thermoplastic elastomer created for the automotive industry. It is specially formulated to have very low fogging characteristics suitable for automotive interior applications.Processing: can be injection molded or extruded on standard thermoplastics equipmentApplications: trinket mats, handbrake grips and gear knobs, pillar trim skins, vent wheels, seat belt scabbards & other seating components, armrest skins, bump stopsFormulated to meet the requirements of automotive Reflectance Fogging test according to SAE J1756
Physical Properties Metric English Comments
Specific Gravity 0.900 g/cc
0.900 g/cc
ISO 1183
Mechanical Properties Metric English Comments
Hardness, Shore A 65
65
ISO 868, 15 sec
Tensile Strength 6.10 MPa
885 psi
500 mm/min, measured parallel to flow; ISO 37
Elongation at Break 400 %
400 %
500 mm/min, measured parallel to flow; ISO 37
100% Modulus 0.00360 GPa
0.522 ksi
500 mm/min, measured parallel to flow; ISO 37
Tear Strength 19.0 kN/m
108 pli
Parallel to flow; ISO 34-B
30.0 kN/m
171 pli
Perpendicular to flow; ISO 34-B
Compression Set 19 %

@Temperature 23.0 °C,
Time 259000 sec
19 %

@Temperature 73.4 °F,
Time 72.0 hour
ISO 815
30 %

@Temperature 70.0 °C,
Time 86400 sec
30 %

@Temperature 158 °F,
Time 24.0 hour
ISO 815
Tensile Set 65 %

@Temperature 70.0 °C,
Time 79200 sec
65 %

@Temperature 158 °F,
Time 22.0 hour
VDA 675 217B
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 165 °C

@Time 10800 sec
329 °F

@Time 3.00 hour
no distortion
Brittleness Temperature -60.0 °C
-76.0 °F
ASTM D 746
Flame Spread 37 mm/min
1.5 in/min
burn rate
Descriptive Properties Value Comments
Fogging, Gravimetric mg DIN 75201B
Fogging, Reflectance % SAE J 1756
Odor rating 2
SAE J1351 / FLTM BO131-01 (dry)
Ozone Resistance 0
100 pphm / 200 hrs / 20% strain