AlphaGary Evoprene™ LF 6152 Automotive Thermoplastic Elastomer

Category	Polymer , Thermoplastic , Elastomer, TPE , Styrenic TPE
Manufacturer	AlphaGary
Trade Name	Evoprene™ LF
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	AlphaGary Evoprene™ LF 6152 Automotive Thermoplastic Elastomer.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Evoprene™ LF is a hydrogenated styrene block copolymer based thermoplastic elastomer created for the automotive industry. It is specially formulated to have very low fogging characteristics suitable for automotive interior applications.Processing: can be injection molded or extruded on standard thermoplastics equipmentApplications: trinket mats, handbrake grips and gear knobs, pillar trim skins, vent wheels, seat belt scabbards & other seating components, armrest skins, bump stopsFormulated to meet the requirements of automotive Reflectance Fogging test according to SAE J1756

Physical Properties	Metric	English	Comments
Specific Gravity	1.03 g/cc	1.03 g/cc	ISO 1183

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	57	57	ISO 868, 15 sec
Tensile Strength	4.50 MPa	653 psi	500 mm/min, measured parallel to flow; ISO 37
Elongation at Break	405 %	405 %	500 mm/min, measured parallel to flow; ISO 37
100% Modulus	0.00240 GPa	0.348 ksi	500 mm/min, measured parallel to flow; ISO 37
Tear Strength	22.0 kN/m	126 pli	Parallel to flow; ISO 34-B
	25.0 kN/m	143 pli	Perpendicular to flow; ISO 34-B
Compression Set	18 % @Temperature 23.0 °C, Time 259000 sec	18 % @Temperature 73.4 °F, Time 72.0 hour	ISO 815
	29 % @Temperature 70.0 °C, Time 86400 sec	29 % @Temperature 158 °F, Time 24.0 hour	ISO 815
Tensile Set	57 % @Temperature 70.0 °C, Time 79200 sec	57 % @Temperature 158 °F, Time 22.0 hour	VDA 675 217B

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Air	165 °C @Time 10800 sec	329 °F @Time 3.00 hour	no distortion
Brittleness Temperature	-60.0 °C	-76.0 °F	ASTM D 746
Flame Spread	46 mm/min	1.8 in/min	burn rate

Descriptive Properties	Value	Comments
Fogging, Reflectance %	SAE J 1756
Odor rating	2	SAE J1351 / FLTM BO131-01 (dry)
Ozone Resistance	0	100 pphm / 200 hrs / 20% strain