Category Metal , Nonferrous Metal , Aluminum Alloy , Aluminum Casting Alloy
Manufacturer Alpase
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Alpase M-5™ Aluminum Mold Plate.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Excellent weldabilitySurface Condition - Machined top and bottom to reduce costly handling and machining stepsDimensional Stability - High dimensional stability during and after machiningPolishing - Good polishing propertiesGood Anodizing and Hard Coating propertiesCorrosion Resistance - Excellent corrosion resistance in many applicationsLow density offers a 5% weight savings over other cast productsVery consistent hardness and mechanical properties throughout its entire thickness range, regardless of size.Vacuum tight microstructureApplications: Injection Molds, Blow Molds, Structural Foam Molds, and Rubber Molds. Additional uses include: Vacuum Forming Tools, Compression Molds, Heating and Cooling Plates and proven Semi-conductor Transfer Chamber applications.Sizes: Thickness up to 30 inches; Width up to 88 inches; Length up to 195 inches. Typical data provided by Alpase.
Physical Properties Metric English Comments
Density 2.66 g/cc
0.0960 lb/in³
2.80 g/cc
0.101 lb/in³
Mechanical Properties Metric English Comments
Hardness, Brinell 70
70
Tensile Strength, Ultimate 283 MPa
41000 psi
Tensile Strength, Yield 124 MPa
18000 psi
Modulus of Elasticity 71.0 GPa
10300 ksi
74.5 GPa
10800 ksi
Thermal Properties Metric English Comments
CTE, linear 23.2 µm/m-°C

@Temperature 20.0 - 100 °C
12.9 µin/in-°F

@Temperature 68.0 - 212 °F
23.8 µm/m-°C

@Temperature 20.0 - 100 °C
13.2 µin/in-°F

@Temperature 68.0 - 212 °F
Thermal Conductivity 139 W/m-K
962 BTU-in/hr-ft²-°F
Electrical Properties Metric English Comments
Electrical Resistivity 0.0000590 ohm-cm
0.0000590 ohm-cm