Aleris Weldural Aluminum Alloy, 600 mm Thickness

Category Metal , Nonferrous Metal , Aluminum Alloy , 2000 Series Aluminum Alloy
Manufacturer Aleris
Trade Name Weldural
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Aleris Weldural Aluminum Alloy, 600 mm Thickness.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Sample treatment not specified for property data.Applications include precise mechanical parts with high dimensional stability, machine components, molds, and refrigeration engineering. Good weldability and machinability. Fair corrosion resistance.
Physical Properties Metric English Comments
Density 2.84 g/cc
0.103 lb/in³
Mechanical Properties Metric English Comments
Hardness, Brinell 130
130
Hardness, Knoop 163
163
Estimated from Brinell
Hardness, Rockwell A 49.4
49.4
Estimated from Brinell
Hardness, Rockwell B 79
79
Estimated from Brinell
Hardness, Vickers 149
149
Estimated from Brinell
Tensile Strength, Ultimate 395 MPa
57300 psi
Typical
Tensile Strength, Yield 315 MPa

@Strain 0.200 %
45700 psi

@Strain 0.200 %
Typical
Elongation at Break 3.5 %
3.5 %
Typical
Modulus of Elasticity 73.8 GPa
10700 ksi
Machinability 70 %
70 %
Thermal Properties Metric English Comments
CTE, linear 22.5 µm/m-°C

@Temperature 20.0 - 100 °C
12.5 µin/in-°F

@Temperature 68.0 - 212 °F
Thermal Conductivity 130 W/m-K
902 BTU-in/hr-ft²-°F
Component Elements Properties Metric English Comments
Aluminum, Al 93 %
93 %
Copper, Cu 5.8 - 6.8 %
5.8 - 6.8 %
Iron, Fe <= 0.40 %
<= 0.40 %
Magnesium, Mg <= 0.10 %
<= 0.10 %
Manganese, Mn 0.20 - 0.40 %
0.20 - 0.40 %
Other, total <= 0.15 %
<= 0.15 %
Silicon, Si <= 0.30 %
<= 0.30 %
Titanium, Ti 0.020 - 0.10 %
0.020 - 0.10 %
Zinc, Zn <= 0.10 %
<= 0.10 %
Zirconium, Zr 0.10 - 0.25 %
0.10 - 0.25 %
Electrical Properties Metric English Comments
Electrical Resistivity 0.00000590 ohm-cm
0.00000590 ohm-cm