Aleris Alustar Aluminum Alloy, MIG-welded

Category Metal , Nonferrous Metal , Aluminum Alloy , 5000 Series Aluminum Alloy
Manufacturer Aleris
Trade Name Alustar
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Aleris Alustar Aluminum Alloy, MIG-welded.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
At least 20% stronger than AA 5083 before and after welding. Bendability and weldability similar to AA 5083. High corrosion resistance. Provides options for ship design and building.Composition differs from standard 5083 and 5383 mainly in terms of higher Mg-content, higher Mn-content, higher Zn-content, and defined Zr-content. The increased Mg-content in the Alustar alloy increases the strength after welding. Together with an increased Mn-content, a higher Mg-content enhances the ductility. To compensate for the deterioration in corrosion resistance caused by the higher Mg-content, an optimal amount of Zn is required. By precipitating Mg-Zn-containing phases in the Al matrix, potential differences between the grain boundaries and grain interiors are eliminated. Zr additions to Alustar alloy cause the formation of a finer grained heat affected zone which leads to a stronger bond in the fusion zone. The effect of Zr is the same in welding wires. Therefore, in addition to the standard filler alloys such as AA5183, Zr-containing filler wires (such as AA 5087) can also be used to weld Alustar alloy plates.
Physical Properties Metric English Comments
Density 2.66 g/cc
0.0961 lb/in³
Aluminum 5083
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate >= 300 MPa
>= 43500 psi
Tensile Strength, Yield >= 160 MPa
>= 23200 psi
Shear Strength 181 MPa
26300 psi
Calculated
Component Elements Properties Metric English Comments
Aluminum, Al 93 %
93 %
Chromium, Cr <= 0.30 %
<= 0.30 %
Copper, Cu <= 0.40 %
<= 0.40 %
Iron, Fe <= 0.50 %
<= 0.50 %
Magnesium, Mg 5.0 - 6.0 %
5.0 - 6.0 %
Manganese, Mn 0.60 - 1.2 %
0.60 - 1.2 %
Silicon, Si <= 0.50 %
<= 0.50 %
Titanium, Ti <= 0.20 %
<= 0.20 %
Zinc, Zn 0.40 - 1.5 %
0.40 - 1.5 %
Zirconium, Zr 0.050 - 0.25 %
0.050 - 0.25 %