Alcoa KAMA 1100 Prime Clear OPS, Sheet (discontinued **)

Category	Polymer , Thermoplastic , Polystyrene (PS)
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Alcoa KAMA 1100 Prime Clear OPS, Sheet (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

CapabilitiesGauge: .005’ to .025” (126 to 635µm)Width: 12” to 62” (305 to 1575mm)Core Size: 6” standard cores, 3” and 8” availableRoll O.D.: 29” standard, up to 40” availableSilicone coating available5 strategic manufacturing locationsPropertiesRemarkable clarityExcellent stiffness to allow downgaugingSuperb yieldEasily thermoformedFDA compliant to CFR 21 #177.1640Kosher MaterialInformation provided by Alcoa Kama Co.

Physical Properties	Metric	English	Comments
Specific Gravity	1.05 g/cc	1.05 g/cc
Thickness	127 - 635 microns	5.00 - 25.0 mil
Linear Mold Shrinkage	0.0050 cm/cm	0.0050 in/in	ASTM D955

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	55.2 - 82.7 MPa	8000 - 12000 psi	ASTM D638
Elongation at Break	3.0 - 10 %	3.0 - 10 %	ASTM D638
Tensile Modulus	2.76 - 3.10 GPa	400 - 450 ksi	ASTM D790

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Air	76.7 °C	170 °F
Minimum Service Temperature, Air	-6.67 °C	20.0 °F

Optical Properties	Metric	English	Comments
Transmission, Visible	90 %	90 %	clear; thickness not quantified

Processing Properties	Metric	English	Comments
Processing Temperature	132 - 154 °C	270 - 310 °F	Thermoforming Temp

Descriptive Properties	Value	Comments
Resistance to Acid	Good to Excellent
Resistance to Alcohols	Good to Excellent
Resistance to Alkalis	Excellent
Resistance to Fat, Grease, and Oil	Good
Resistance to Hydrocarbon Solvents	Poor
Resistance to Strong Oxidizers	Poor
Yield, in²/lb/mil	26360