Advanced Polymer Alloys DuraGrip™ 6165 TR Thermoplastic Elastomer

Category Polymer , Thermoplastic , Elastomer, TPE
Manufacturer APA - Advanced Polymer Alloys
Trade Name DuraGrip™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Advanced Polymer Alloys DuraGrip™ 6165 TR Thermoplastic Elastomer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
DuraGrip® DGR6165TR is a translucent thermoplastic elastomer (TPE) formulated for excellent elastic properties and enhanced adhesion to engineered thermoplastics using insert molding, co-injection molding and co-extrusion processes. DGR6165TR bonds tenaciously to polycarbonate, polycarbonate alloys, ABS, ASA, acrylics, and cellulosic materials. It will also bond to various nylons and PET. DGR6165TR is hygroscopic and drying is recommended at 150F for 3 to 4 hours to ensure optimum aesthetics, properties and adhesion.Information provided by Advanced Polymer Alloys
Physical Properties Metric English Comments
Specific Gravity 1.04 g/cc
1.04 g/cc
ASTM D471
Viscosity 427000 cP

@Shear Rate 294 1/s,
Temperature 190 °C
427000 cP

@Shear Rate 294 1/s,
Temperature 374 °F
ASTM D3835
Melt Index of Compound 11 g/10 min

@Load 8.70 kg,
Temperature 190 °C
11 g/10 min

@Load 19.2 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Shore A 65
65
10 Sec; ASTM D2240
Tensile Strength at Break 18.11 MPa
2627 psi
Parallel Flow; ASTM D412
25.88 MPa
3754 psi
Perpendicular Flow; ASTM D412
Elongation at Break 583 %
583 %
Parallel Flow; ASTM D412
810 %
810 %
Perpendicular Flow; ASTM D573
100% Modulus 0.00343 GPa
0.498 ksi
Parallel Flow; ASTM D412
0.00396 GPa
0.575 ksi
Perpendicular Flow; ASTM D412
300% Modulus 0.007729 GPa
1.121 ksi
Parallel Flow; ASTM D412
0.009225 GPa
1.338 ksi
Perpendicular Flow; ASTM D412
Graves Tear Strength 52.2 kN/m
298 pli
Die C, parallel flow; ASTM D624
59.6 kN/m
340 pli
Die C, perpendicular flow; ASTM D624
Processing Properties Metric English Comments
Melt Temperature 180 - 230 °C