Advanced Elastomer Systems VistaFlex® 715-B Thermoplastic Rubber  (discontinued **)

Category Polymer , Thermoplastic , Elastomer, TPE , Thermoplastic Elastomer, Melt-Processible Rubber
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Advanced Elastomer Systems VistaFlex® 715-B Thermoplastic Rubber  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: A black high-flow thermoplastic elastomer especially designed for injection molding applications. It replaces soft thermoplastics such as SBS, SEBS, and PVC blends. Supplied as free-flowing pellets in 25 kilogram (55 pound) moisture barrier bags.Features: High flowGood surface appearance on molded partsGood tensile properties and high elongation at breakGood tear strengthProduct Notes: Values are for injection molded plaques, side gated.82.6 mm x 117.5 mm x 3 mmInformation provided by Advanced Elastomer Systems.Advanced Elastomer Systems is now a part of ExxonMobil. This grade was removed from the Advanced Elastomers Systems standard product line before the ExxonMobil acquisiton.
Physical Properties Metric English Comments
Density 1.05 g/cc
0.0379 lb/in³
ASTM D792
Melt Flow 35 g/10 min

@Load 5.00 kg,
Temperature 230 °C
35 g/10 min

@Load 11.0 lb,
Temperature 446 °F
Mechanical Properties Metric English Comments
Hardness, Shore A 85
85
5 seconds; ASTM D2240
Tensile Strength at Break 4.479 MPa
649.6 psi
After 3000 hrs. Xenon test 1200; ISO 4665
6.40 MPa
928 psi
Across flow; ASTM D412
Tensile Strength, Yield 4.10 MPa
595 psi
At 100% elongation, across flow; ASTM D412
Elongation at Break 525 %
525 %
After 3000 hrs. Xenon test 1200; ISO 4665
700 %
700 %
Across flow; ASTM D412
Tensile Modulus 0.110 GPa
16.0 ksi
1mm/min; DIN 53457
Flexural Modulus 0.105 GPa
15.2 ksi
1.7 mm/min; DIN 53457
Izod Impact, Notched NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
ISO 180A
Tear Strength 49.1 kN/m
280 pli
73°F; ASTM D624
Compression Set 38 %
38 %
73°F, 22 hr, Method B; ASTM D395
55 %
55 %
158°F, 22 hr, Method B; ASTM D395
Thermal Properties Metric English Comments
Vicat Softening Point 53.0 °C
127 °F
Vicat A, 1 kg; DIN 53460/ISO 306
Brittleness Temperature -50.0 °C
-58.0 °F
ASTM D746
Processing Properties Metric English Comments
Processing Temperature 175 - 240 °C
347 - 464 °F
Mold Temperature 20.0 - 40.0 °C
68.0 - 104 °F