Addiplast Addinyl A2 E Flame Retardant Nylon 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Unreinforced, Flame Retardant |
| Manufacturer | Addiplast |
| Trade Name | Addinyl |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Addiplast Addinyl A2 E Flame Retardant Nylon 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Flame retardant, halogen freeInformation provided by Addiplast.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | ISO 1183/A |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 78 | 78 | Conditioned; ISO 868 |
| 85 | 85 | ISO 868 | |
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | Conditioned; ISO R 527 |
| 85.0 MPa | 12300 psi | ISO R 527 | |
| Elongation at Break | 30 % | 30 % | ISO R 527 |
| >= 50 % | >= 50 % | Conditioned; ISO R 527 | |
| Modulus of Elasticity | 1.30 GPa | 189 ksi | Conditioned; ISO 178 |
| 2.90 GPa | 421 ksi | ISO 178 | |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | ISO 180/1A |
| 12.0 kJ/m² | 5.71 ft-lb/in² | Conditioned; ISO 180/1A | |
| Charpy Impact Unnotched | NB | NB | ISO 179/IeU |
| NB | NB | Conditioned; ISO 179/IeU | |
| Charpy Impact, Notched | 0.500 J/cm² | 2.38 ft-lb/in² | ISO 179/IeA |
| 1.10 J/cm² | 5.23 ft-lb/in² | Conditioned; ISO 179/IeA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 260 °C | 500 °F | ISO 3146/C2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C | 185 °F | ISO 75-2/AF |
| Flammability, UL94 | V-2 @Thickness 1.60 mm |
V-2 @Thickness 0.0630 in |
|
| Oxygen Index | 28 % | 28 % | ISO 4589 |
| Glow Wire Test | 960 °C | 1760 °F | CEI 60695/2/1 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | Conditioned; CEI 60093 |
| 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | CEI 60093 | |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | Conditioned; CEI 60093 |
| 1.00e+15 ohm | 1.00e+15 ohm | CEI 60093 | |
| Dielectric Strength | 28.0 kV/mm | 711 kV/in | CEI 60243-1 |
| Comparative Tracking Index | >= 600 V | >= 600 V | CEI 60112/Solution A |
Users viewing this material also viewed the following:
- Potters Industries Conduct-O-Fil® S4000-S3 Silver-Coated Solid Glass Spheres
- Albis Plastics EVA Masterbatch MB 50 Black (discontinued **)
- DSM Akulon® S223-P2 Impact Modified Nylon 66 (European Grade) (Dry) (discontinued **)
- Karina E KAPU 6048/1D Compound PVC Black
- Johnson Matthey HC Platinum w/ 5% Cobalt Jewelry Alloy
- SABIC Innovative Plastics PC0703R PC
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 60 PHR N220 (ISAF) Filler
- Master Bond EP21HT High Temperature Resistant Two Component Epoxy
- Entec Hylex® P1010FR Polycarbonate
- 3M Dyneon™ FE 5522 Fluoroelastomer
Copyright © lookpolymers.com All Rights Reserved