Aclo Accutech Polypropylene Copolymer CP0437M10L Mica Reinforced
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 10% Mica Filler |
| Manufacturer | Aclo Compounders |
| Trade Name | Accutech |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aclo Accutech Polypropylene Copolymer CP0437M10L Mica Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.950 g/cc | 0.0343 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.010 cm/cm | 0.010 in/in | MD; ASTM D955 |
| Melt Flow | 19 g/10 min | 19 g/10 min | ASTM D1238 |
| Ash | 10 % | 10 % | ASTM D2584 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 51 | 51 | ASTM D785 |
| Tensile Strength at Break | 13.0 MPa | 1890 psi | ASTM D638 |
| Tensile Strength, Yield | 17.0 MPa | 2470 psi | ASTM D638 |
| Elongation at Break | 27 % | 27 % | ASTM D638 |
| Elongation at Yield | 5.0 % | 5.0 % | ASTM D638 |
| Tensile Modulus | 1.100 GPa | 159.5 ksi | ASTM D638 |
| Flexural Strength | 21.0 MPa | 3050 psi | ASTM D790 |
| Flexural Modulus | 1.100 GPa | 159.5 ksi | ASTM D790 |
| Izod Impact, Notched | 2.99 J/cm | 5.60 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 80.0 °C | 176 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 48.9 °C | 120 °F |
Users viewing this material also viewed the following:
- Plastics Group Polifil® RMC-20V 20% Calcium Carbonate-Reinforced Polypropylene, High Impact, UV Stabilized
- Universal Wire Works E81T1-B2 Flux Cored Carbon Steel Tubular Electrode
- Dow Corning RM 2051 THICKENING AGENT
- Cytec Thornel® T-50 3K Carbon Fiber, Polyacrylonitrile (PAN) Precursor
- Dow TUFLIN™ HS-7021 NT 7 Linear Low Density Polyethylene Resin
- Asahi Kasei Tenac® 5010 Homopolymer Acetal Resin
- 3M OFM0103 Outdoor UL Recognized Polyester Overlaminate Label Products
- Unipetrol PP MONSTEN® FC 908 Polypropylene Random Copolymer
Copyright © lookpolymers.com All Rights Reserved