Aclo Accutech Polypropylene Copolymer CP0436G30CL Glass Reinforced
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 30% Glass Fiber Filler |
| Manufacturer | Aclo Compounders |
| Trade Name | Accutech |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aclo Accutech Polypropylene Copolymer CP0436G30CL Glass Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.10 g/cc | 0.0397 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0010 cm/cm | 0.0010 in/in | MD; ASTM D955 |
| Melt Flow | 4.0 g/10 min | 4.0 g/10 min | ASTM D1238 |
| Ash | 30 % | 30 % | ASTM D2584 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 92 | 92 | ASTM D785 |
| Tensile Strength at Break | 50.0 MPa | 7250 psi | ASTM D638 |
| Tensile Strength, Yield | 51.0 MPa | 7400 psi | ASTM D638 |
| Elongation at Break | 8.0 % | 8.0 % | ASTM D638 |
| Elongation at Yield | 5.0 % | 5.0 % | ASTM D638 |
| Tensile Modulus | 2.250 GPa | 326.3 ksi | ASTM D638 |
| Flexural Strength | 75.98 MPa | 11020 psi | ASTM D790 |
| Flexural Modulus | 4.149 GPa | 601.8 ksi | ASTM D790 |
| Izod Impact, Notched | 1.66 J/cm | 3.10 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 157 °C | 315 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 134 °C | 273 °F |
Users viewing this material also viewed the following:
- Ovation Polymers Nima™ NH PA66UT Nylon 66
- Invista 1102 PET Copolymer Packaging Resin (discontinued **)
- Kolon KOCETAL® CF704 Conductive Grade Acetal Resin
- Gwent Electronic Materials C2080211P2 High Brightness Phosphor Ink (Blue/Green & Blue)
- Lehmann & Voss LUVOCOM® 1301-7575 PPS, linear, with glass fiber
- A. Schulman FORMION™ FI 341 Ionomer
- Hexcel® Redux® 312L Modified epoxy film adhesive
- Hexcel® HexPly® M34 75°C (167°F) Curing Epoxy Matrix, E-glass Balanced Fabric 600 g/m2
- Loctite® 3035™ Polyolefin Bonder
- Dow H110-02NZ Polypropylene Homopolymer Resin
Copyright © lookpolymers.com All Rights Reserved