Aclo Accutech Polypropylene CP0437T40V Copolymer Talc Reinforced
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 40% Talc Filler |
| Manufacturer | Aclo Compounders |
| Trade Name | Accutech |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aclo Accutech Polypropylene CP0437T40V Copolymer Talc Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Approved to GMP.PP.079 Black A12566
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.23 g/cc | 0.0444 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0060 cm/cm | 0.0060 in/in | ASTM D955 |
| Melt Flow | 12 g/10 min | 12 g/10 min | ASTM D1238 |
| Ash | 37 - 43 % | 37 - 43 % | ASTM D2584 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 87 | 87 | ASTM D785 |
| Tensile Strength, Yield | 29.6 MPa | 4300 psi | ASTM D638 |
| Elongation at Break | 20 % | 20 % | ASTM D638 |
| Tensile Modulus | 3.10 GPa | 450 ksi | ASTM D638 |
| Flexural Strength | 51.7 MPa | 7500 psi | ASTM D790 |
| Flexural Modulus | 3.80 GPa | 551 ksi | ASTM D790 |
| Izod Impact, Notched | 0.427 J/cm | 0.800 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 135 °C | 275 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 77.8 °C | 172 °F |
Users viewing this material also viewed the following:
- Solvay Engineered Polymers SEQUEL® 1440LS TPO (discontinued **)
- Eastman M30036-P Polyethylene (discontinued **)
- Teknor Apex Sinvicomp SGH 2800 Polyvinyl Chloride, Flexible
- TIMCAL ENSACO™ 210G Conductive Carbon Black
- ExxonMobil Mobil Clean 5W-30 Motor Oil
- Covestro Bayblend® KU 2-1474 Polycarbonate/ABS Blend
- Barlog Plastics KEBAFLEX SG 40 A.01 black TPE-S, Shore A40, black
- Arkema Group KYNAR FLEX® 2950-05 Polyvinylidene Fluoride Copolymer - Extrusion & Molding
- Arkema Group VOLTALEF® 302 PCTFE
- Kennametal Stellite Stellite® 31 PM cast aged 8 hours at 802°C air cooled
Copyright © lookpolymers.com All Rights Reserved