- Aclo Accuguard Polypropylene HP1362V2CSL Homopolymer Flame Retardant Copper Stabilized
Aclo Accuguard Polypropylene HP1362V2CSL Homopolymer Flame Retardant Copper Stabilized
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Flame Retardant |
| Manufacturer | Aclo Compounders |
| Trade Name | Accuguard |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aclo Accuguard Polypropylene HP1362V2CSL Homopolymer Flame Retardant Copper Stabilized.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.935 g/cc | 0.0338 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.013 cm/cm | 0.013 in/in | ASTM D955 |
| Melt Flow | 6.0 g/10 min | 6.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 200 MPa | 29000 psi | ASTM D638 |
| Tensile Strength, Yield | 35.0 MPa | 5080 psi | ASTM D638 |
| Tensile Modulus | 1.20 GPa | 174 ksi | ASTM D638 |
| Flexural Strength | 42.0 MPa | 6090 psi | ASTM D790 |
| Flexural Modulus | 1.40 GPa | 203 ksi | ASTM D790 |
| Izod Impact, Notched | 0.481 J/cm | 0.900 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 95.0 °C | 203 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 57.8 °C | 136 °F | |
| UL RTI, Electrical | 110 °C | 230 °F | |
| UL RTI, Mechanical with Impact | 110 °C | 230 °F | |
| UL RTI, Mechanical without Impact | 110 °C | 230 °F | |
| Flammability, UL94 | V-2 @Thickness 1.59 mm |
V-2 @Thickness 0.0625 in |
UL File #E99379 |
Users viewing this material also viewed the following:
- Polymer Resources PC/ABS-FR1-[color]-3 PC Blend, Flame Retardant, Standard Flow, UV Stabilized
- Plastcom SLOVAMID 6 BT LS Polyamide 6, UV Stabilized
- ICO Polymers ICORENEâ„¢ 190-1327 LMDPE Rotational Molding Resin
- Haynes 214® alloy, 30% cold reduction, 925°C for 5 minutes
- Mitsui APELâ„¢ APL6509T Cyclo Olefin Copolymer (COC)
- Solvay Specialty Polymers Catalyst CT/2 Polyolefin
- Wellman Wellamid® GFX1717-BK1 Nylon 66, 43% Glass Fiber Reinforced, Silicone Lubricated
- Dow Corning SYL-OFF® 1171A CATALYST
- Polyram PlusTek RA321G6 Nylon 6.6, 30% Glass Fiber, Flame Retardant
Copyright © lookpolymers.com All Rights Reserved