Aclo Accuguard Polypropylene CP0467V0CSL Copolymer Flame Retardant Copper Stabilized
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Flame Retardant |
| Manufacturer | Aclo Compounders |
| Trade Name | Accuguard |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aclo Accuguard Polypropylene CP0467V0CSL Copolymer Flame Retardant Copper Stabilized.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.32 g/cc | 0.0477 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0090 cm/cm | 0.0090 in/in | MD; ASTM D955 |
| Melt Flow | 3.0 g/10 min | 3.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 70 | 70 | ASTM D785 |
| Tensile Strength at Break | 15.0 MPa | 2180 psi | ASTM D638 |
| Tensile Strength, Yield | 26.0 MPa | 3770 psi | ASTM D638 |
| Elongation at Break | 25 % | 25 % | ASTM D638 |
| Elongation at Yield | 4.0 % | 4.0 % | ASTM D638 |
| Tensile Modulus | 2.299 GPa | 333.5 ksi | ASTM D638 |
| Flexural Strength | 39.0 MPa | 5660 psi | ASTM D790 |
| Flexural Modulus | 2.299 GPa | 333.5 ksi | ASTM D790 |
| Izod Impact, Notched | 0.641 J/cm | 1.20 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 101 °C | 214 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F | |
| Flammability, UL94 | V-0 @Thickness 1.59 mm |
V-0 @Thickness 0.0625 in |
UL File #E99379(N) |
Users viewing this material also viewed the following:
- SABIC PVC 67S Suspension Polyvinyl Chloride for Rigid Extruded Products
- Lehmann & Voss LUVOCOM® 80/TF/18/NT Polyacetal-copolymer, with PTFE
- Mitsubishi Hostaphan® WN, 250 micron Nominal Thickness Translucent White Polyethylene Terephthalate Film
- H.C. Starck 4201 Pure Tungsten WF-3, Foil
- Samsung Cheil Industries Starex® LX-0951 ABS, Unreinforced Metallic-Look
- Teknor Apex APEX® 80853-B Polyvinyl Chloride, Flexible
- Total EVA 1040 VN 4 Ethylene Vinyl Acetate Copolymer - Blown Film
- Eagle Brass 200/201 Nickel Alloy, Annealed
- 3M FV026505 White Vinyl Label Products
- S&E Specialty Polymers XP11-289A1MG PVC
Copyright © lookpolymers.com All Rights Reserved