Abatron AboCast/AboCure 8110-3 Flexible Epoxy

Category Polymer , Adhesive , Thermoset , Epoxy , Epoxy Adhesive, Flexible
Manufacturer Abatron
Trade Name AboCast/AboCure
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Abatron AboCast/AboCure 8110-3 Flexible Epoxy.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This epoxy system can achieve flexibility and plasticity without sacrificing adhesive, electrical, structural, and other properties. This compound is a clear (unfilled) basic formulation. Its applications include: bonding, laminating, casting, embedding, electrical potting, impregnating, coating, etc. It can be supplied in several variations to modify viscosity, reaction rate, color, most physical and chemical properties, and with many fillers to meet most requirements.
Physical Properties Metric English Comments
Water Absorption 4.5 %

@Time 2.59e+6 sec
4.5 %

@Time 720 hour
immersion; cured 30 days @ 25°C
4.5 %

@Time 2.59e+6 sec
4.5 %

@Time 720 hour
immersion; cured 90 days @ 25°C
4.9 %

@Time 7200 sec
4.9 %

@Time 2.00 hour
boil; cured 2 hours @ 93°C
5.3 %

@Time 2.59e+6 sec
5.3 %

@Time 720 hour
immersion; cured 7 days @ 25°C
Viscosity 1270 cP
1270 cP
Mechanical Properties Metric English Comments
Hardness, Shore A 40

@Temperature 75.0 °C
40

@Temperature 167 °F
cured 2 hrs. @ 93°C
47

@Temperature 75.0 °C
47

@Temperature 167 °F
cured 7 days @ 25°C
80

@Temperature 25.0 °C
80

@Temperature 77.0 °F
cured 2 hrs. @ 93°C
86

@Temperature 25.0 °C
86

@Temperature 77.0 °F
cured 7 days @ 25°C
98

@Temperature 0.000 °C
98

@Temperature 32.0 °F
cured 7 days @ 25°C
Hardness, Shore D 80

@Temperature 0.000 °C
80

@Temperature 32.0 °F
cured 2 hrs. @ 93°C
85

@Temperature -60.0 °C
85

@Temperature -76.0 °F
cured 7 days @ 25°C
85

@Temperature -60.0 °C
85

@Temperature -76.0 °F
cured 2 hrs. @ 93°C
Tensile Strength, Ultimate 1.69 MPa
245 psi
cured 7 days @ 25°C
1.69 MPa
245 psi
cured 30 days @ 25°C
1.79 MPa
260 psi
cured 90 days @ 25°C
1.90 MPa
275 psi
cured 2 hours @ 93°C
Elongation at Break 130 %
130 %
cured 90 days @ 25°C
140 %
140 %
cured 7 days @ 25°C
145 %
145 %
cured 30 days @ 25°C
160 %
160 %
cured 2 hours @ 93°C
Shear Strength 4.48 MPa

@Temperature 0.000 °C
650 psi

@Temperature 32.0 °F
Tensile, Al/Al lap joint; cured 7 days @ 25°C
5.52 MPa

@Temperature 25.0 °C
800 psi

@Temperature 77.0 °F
Tensile, Al/Al lap joint; cured 2 hours @ 93°C
7.24 MPa

@Temperature 25.0 °C
1050 psi

@Temperature 77.0 °F
Tensile, Al/Al lap joint; cured 90 days @ 25°C
7.31 MPa

@Temperature 25.0 °C
1060 psi

@Temperature 77.0 °F
Tensile, Al/Al lap joint; cured 30 days @ 25°C
Electrical Properties Metric English Comments
Volume Resistivity 2.70e+9 ohm-cm

@Temperature 25.0 °C
2.70e+9 ohm-cm

@Temperature 77.0 °F
cured 2 hours @ 93°C
1.40e+10 ohm-cm

@Temperature 25.0 °C
1.40e+10 ohm-cm

@Temperature 77.0 °F
cured 30 days @ 25°C
4.80e+10 ohm-cm

@Temperature 25.0 °C
4.80e+10 ohm-cm

@Temperature 77.0 °F
cured 7 days @ 25°C
6.40e+10 ohm-cm

@Temperature 25.0 °C
6.40e+10 ohm-cm

@Temperature 77.0 °F
cured 90 days @ 25°C
Processing Properties Metric English Comments
Pot Life 35 min

@Temperature 25.0 °C
35 min

@Temperature 77.0 °F
200 g
Descriptive Properties Value Comments
Parts by Weight (pbw) 100
AboCast 8110-3
11
AboCure 8110-3