Abatron AboCast/AboCure 8110-2 Flexible Epoxy

Category Polymer , Adhesive , Thermoset , Epoxy , Epoxy Adhesive, Flexible
Manufacturer Abatron
Trade Name AboCast/AboCure
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Abatron AboCast/AboCure 8110-2 Flexible Epoxy.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This epoxy system can achieve flexibility and plasticity without sacrificing adhesive, electrical, structural, and other properties. This compound is a clear (unfilled) basic formulation. Its applications include: bonding, laminating, casting, embedding, electrical potting, impregnating, coating, etc. It can be supplied in several variations to modify viscosity, reaction rate, color, most physical and chemical properties, and with many fillers to meet most requirements.
Physical Properties Metric English Comments
Water Absorption 3.3 %

@Time 2.59e+6 sec
3.3 %

@Time 720 hour
immersion; cured 7 days @ 25°C
3.3 %

@Time 2.59e+6 sec
3.3 %

@Time 720 hour
immersion; cured 30 days @ 25°C
Viscosity 2260 cP
2260 cP
Mechanical Properties Metric English Comments
Hardness, Shore D 33

@Temperature 75.0 °C
33

@Temperature 167 °F
cured 7 days @ 25°C
42

@Temperature 75.0 °C
42

@Temperature 167 °F
cured 30 days @ 25°C
82

@Temperature 25.0 °C
82

@Temperature 77.0 °F
cured 7 days @ 25°C
84

@Temperature 25.0 °C
84

@Temperature 77.0 °F
cured 30 days @ 25°C
86

@Temperature 0.000 °C
86

@Temperature 32.0 °F
cured 30 days @ 25°C
87

@Temperature 0.000 °C
87

@Temperature 32.0 °F
cured 7 days @ 25°C
89

@Temperature -60.0 °C
89

@Temperature -76.0 °F
cured 7 days @ 25°C
89

@Temperature -60.0 °C
89

@Temperature -76.0 °F
cured 30 days @ 25°C
Tensile Strength, Ultimate 45.68 MPa
6625 psi
cured 7 days @ 25°C
48.6 MPa
7050 psi
cured 30 days @ 25°C
Elongation at Break 12 %
12 %
cured 30 days @ 25°C
20 %
20 %
cured 7 days @ 25°C
Shear Strength 2.55 MPa

@Temperature 75.0 °C
370 psi

@Temperature 167 °F
Tensile, Al/Al lap joint; cured 7 days @ 25°C
27.2 MPa

@Temperature 25.0 °C
3950 psi

@Temperature 77.0 °F
Tensile, Al/Al lap joint; cured 7 days @ 25°C
30.3 MPa

@Temperature 0.000 °C
4400 psi

@Temperature 32.0 °F
Tensile, Al/Al lap joint; cured 7 days @ 25°C
Electrical Properties Metric English Comments
Volume Resistivity 4.60e+9 ohm-cm

@Temperature 100 °C
4.60e+9 ohm-cm

@Temperature 212 °F
cured 30 days @ 25°C
1.70e+10 ohm-cm

@Temperature 100 °C
1.70e+10 ohm-cm

@Temperature 212 °F
cured 7 days @ 25°C
3.30e+14 ohm-cm

@Temperature 25.0 °C
3.30e+14 ohm-cm

@Temperature 77.0 °F
cured 30 days @ 25°C
7.10e+14 ohm-cm

@Temperature 25.0 °C
7.10e+14 ohm-cm

@Temperature 77.0 °F
cured 7 days @ 25°C
Processing Properties Metric English Comments
Pot Life 40 min

@Temperature 25.0 °C
40 min

@Temperature 77.0 °F
200 g
Descriptive Properties Value Comments
Parts by Weight (pbw) 100
AboCast 8110-2
16.5
AboCure 8110-2