Abatron AboCast 8110-6/AboCure 8110-1 Flexible Epoxy

Category Polymer , Adhesive , Thermoset , Epoxy , Epoxy Adhesive, Flexible
Manufacturer Abatron
Trade Name AboCast
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Abatron AboCast 8110-6/AboCure 8110-1 Flexible Epoxy.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This epoxy system can achieve flexibility and plasticity without sacrificing adhesive, electrical, structural, and other properties. This compound is a clear (unfilled) basic formulation. Its applications include: bonding, laminating, casting, embedding, electrical potting, impregnating, coating, etc. It can be supplied in several variations to modify viscosity, reaction rate, color, most physical and chemical properties, and with many fillers to meet most requirements.
Physical Properties Metric English Comments
Water Absorption 2.5 %

@Time 7200 sec
2.5 %

@Time 2.00 hour
boil; cured 2 hours @ 93°C
Viscosity 2000 cP
2000 cP
Mechanical Properties Metric English Comments
Hardness, Shore D 75

@Temperature 75.0 °C
75

@Temperature 167 °F
cured 2 hrs. @ 93°C
83

@Temperature 25.0 °C
83

@Temperature 77.0 °F
cured 2 hrs. @ 93°C
87

@Temperature 0.000 °C
87

@Temperature 32.0 °F
cured 2 hrs. @ 93°C
90

@Temperature -60.0 °C
90

@Temperature -76.0 °F
cured 2 hrs. @ 93°C
Tensile Strength, Ultimate 43.33 MPa
6285 psi
cured 2 hours @ 93°C
58.16 MPa
8435 psi
cured 8 hours @ 93°C
Elongation at Break 11 %
11 %
cured 8 hours @ 93°C
13 %
13 %
cured 2 hours @ 93°C
Shear Strength 12.2 MPa

@Temperature 75.0 °C
1770 psi

@Temperature 167 °F
Tensile, Al/Al lap joint; cured 2 hours @ 93°C
28.9 MPa

@Temperature 0.000 °C
4190 psi

@Temperature 32.0 °F
Tensile, Al/Al lap joint; cured 2 hours @ 93°C
41.9 MPa

@Temperature 25.0 °C
6080 psi

@Temperature 77.0 °F
Tensile, Al/Al lap joint; cured 2 hours @ 93°C
Electrical Properties Metric English Comments
Volume Resistivity 7.90e+7 ohm-cm

@Temperature 150 °C
7.90e+7 ohm-cm

@Temperature 302 °F
cured 2 hours @ 93°C
7.70e+8 ohm-cm

@Temperature 112 °C
7.70e+8 ohm-cm

@Temperature 234 °F
cured 2 hours @ 93°C
2.70e+9 ohm-cm

@Temperature 100 °C
2.70e+9 ohm-cm

@Temperature 212 °F
cured 2 hours @ 93°C
9.40e+14 ohm-cm

@Temperature 25.0 °C
9.40e+14 ohm-cm

@Temperature 77.0 °F
cured 2 hours @ 93°C
Processing Properties Metric English Comments
Pot Life 22 min

@Temperature 25.0 °C
22 min

@Temperature 77.0 °F
200 g
Gel Time 6.00 min

@Temperature 93.0 °C
6.00 min

@Temperature 199 °F
10 g
Descriptive Properties Value Comments
Parts by Weight (pbw) 10.2
AboCure 8110-1
100
AboCast 8110-6