Abatron AboCast 8110-5/AboCure 8110-1 Flexible Epoxy

Category Polymer , Adhesive , Thermoset , Epoxy , Epoxy Adhesive, Flexible
Manufacturer Abatron
Trade Name AboCast
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Abatron AboCast 8110-5/AboCure 8110-1 Flexible Epoxy.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This epoxy system can achieve flexibility and plasticity without sacrificing adhesive, electrical, structural, and other properties. This compound is a clear (unfilled) basic formulation. Its applications include: bonding, laminating, casting, embedding, electrical potting, impregnating, coating, etc. It can be supplied in several variations to modify viscosity, reaction rate, color, most physical and chemical properties, and with many fillers to meet most requirements.
Physical Properties Metric English Comments
Water Absorption 2.3 %

@Time 7200 sec
2.3 %

@Time 2.00 hour
boil; cured 2 hours @ 93°C
Viscosity 1650 cP
1650 cP
Mechanical Properties Metric English Comments
Hardness, Shore D 76

@Temperature 75.0 °C
76

@Temperature 167 °F
cured 2 hrs. @ 93°C
85

@Temperature 25.0 °C
85

@Temperature 77.0 °F
cured 2 hrs. @ 93°C
87

@Temperature 0.000 °C
87

@Temperature 32.0 °F
cured 2 hrs. @ 93°C
90

@Temperature -60.0 °C
90

@Temperature -76.0 °F
cured 2 hrs. @ 93°C
Tensile Strength, Ultimate 68.64 MPa
9955 psi
cured 2 hours @ 93°C
72.19 MPa
10470 psi
cured 8 hours @ 93°C
Elongation at Break 6.4 %
6.4 %
cured 8 hours @ 93°C
9.8 %
9.8 %
cured 2 hours @ 93°C
Shear Strength 23.2 MPa

@Temperature 75.0 °C
3370 psi

@Temperature 167 °F
Tensile, Al/Al lap joint; cured 2 hours @ 93°C
25.2 MPa

@Temperature 0.000 °C
3650 psi

@Temperature 32.0 °F
Tensile, Al/Al lap joint; cured 2 hours @ 93°C
33.2 MPa

@Temperature 25.0 °C
4810 psi

@Temperature 77.0 °F
Tensile, Al/Al lap joint; cured 2 hours @ 93°C
Electrical Properties Metric English Comments
Volume Resistivity 2.00e+9 ohm-cm

@Temperature 150 °C
2.00e+9 ohm-cm

@Temperature 302 °F
cured 2 hours @ 93°C
3.20e+9 ohm-cm

@Temperature 112 °C
3.20e+9 ohm-cm

@Temperature 234 °F
cured 2 hours @ 93°C
4.10e+10 ohm-cm

@Temperature 100 °C
4.10e+10 ohm-cm

@Temperature 212 °F
cured 2 hours @ 93°C
1.80e+16 ohm-cm

@Temperature 25.0 °C
1.80e+16 ohm-cm

@Temperature 77.0 °F
cured 2 hours @ 93°C
Processing Properties Metric English Comments
Pot Life 19 min

@Temperature 25.0 °C
19 min

@Temperature 77.0 °F
200 g
Gel Time 2.00 min

@Temperature 93.0 °C
2.00 min

@Temperature 199 °F
10 g
Descriptive Properties Value Comments
Parts by Weight (pbw) 100
AboCast 8110-5
11.6
AboCure 8110-1