Abatron AboCast 7802-1/AboCure 7804-3 (80 pbw) Epoxy

Category Polymer , Adhesive , Thermoset , Epoxy , Epoxy, Cast, Unreinforced
Manufacturer Abatron
Trade Name AboCast
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Abatron AboCast 7802-1/AboCure 7804-3 (80 pbw) Epoxy.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
AboCast 7802-1 is a clear resin with low viscosity (600-800 cps.) and a weight of 9.1 lbs/gallon. AboCure 7804-3 a clear, slightly accelerated converter for lower rigidity. It has an HDT of 60°C, variable ratio, a viscosity of 300 cps., and a weight of 7.8 lbs/gallon. AboCast 7802-1/AboCure 7804-3 has versatility, many variable-ratio possibilities, and a tenacious adhesion to metals, ceramics, glass, wood, and most rigid materials which permits permanent structural and dielectric bonds. Absence of volatiles and minimum shrinkage, typical of solventless epoxy systems, allow castings and masses of virtually any desired thickness. Suggested Uses: Multi-purpose casting, coating, and bonding for applications requiring high dielectric resistance, structural strength, and radiation resistance as well as resistance to weather, water, alkalis, diluted acids, fuels, and most common solvents; it was originally developed for FERMILAB.
Physical Properties Metric English Comments
Density 0.935 g/cc
0.0338 lb/in³
AboCure 7804-3
1.09 g/cc
0.0394 lb/in³
AboCast 7802-1
Water Absorption 0.20 - 0.40 %
0.20 - 0.40 %
Viscosity 350 - 500 cP
350 - 500 cP
blended
Mechanical Properties Metric English Comments
Hardness, Shore D 60

@Temperature 100 °C,
Time 10800 sec
60

@Temperature 212 °F,
Time 3.00 hour
60

@Temperature 100 °C,
Time 10800 sec
60

@Temperature 212 °F,
Time 3.00 hour
1/8 in thickness
25

@Time 86400 sec
25

@Time 24.0 hour
1/8 in thickness
40

@Time 259000 sec
40

@Time 72.0 hour
1/8 in thickness
50

@Time 86400 sec
50

@Time 24.0 hour
60

@Time 259000 sec
60

@Time 72.0 hour
Tensile Strength at Break 13.8 - 27.6 MPa
2000 - 4000 psi
Elongation at Break >= 20 %
>= 20 %
Flexural Strength 13.8 - 20.7 MPa
2000 - 3000 psi
Compressive Strength 20.7 - 27.6 MPa
3000 - 4000 psi
Electrical Properties Metric English Comments
Dielectric Strength 11.8 - 15.7 kV/mm
300 - 400 kV/in
Processing Properties Metric English Comments
Pot Life 120 min
120 min
100 g
Descriptive Properties Value Comments
Parts by Weight (pbw) 100
AboCast 7802-1
80
AboCure 7804-3