- Aaron Industries AAROPRENE® TFIPP 2030 High Impact Talc Filled Polypropylene
Aaron Industries AAROPRENE® TFIPP 2030 High Impact Talc Filled Polypropylene
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 40% Talc Filler |
| Manufacturer | Aaron Industries Corporation |
| Trade Name | AAROPRENE® TFIPP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aaron Industries AAROPRENE® TFIPP 2030 High Impact Talc Filled Polypropylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
AAROPRENE® TFIPP 2000 Series Reinforced CompoundsMelt flow index may be specified. Color may be specified.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.14 g/cc | 1.14 g/cc | ASTM D792 |
| Filler Content | 30 % | 30 % | Talc; ASTM D2584 |
| Linear Mold Shrinkage | 0.011 cm/cm | 0.011 in/in | ASTM D955 |
| Melt Flow | 8.0 - 12 g/10 min @Load 2.16 kg, Temperature 230 °C |
8.0 - 12 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 27.2 MPa | 3950 psi | ASTM D638 |
| Flexural Modulus | 2.41 GPa | 350 ksi | ASTM D790 |
| Izod Impact, Notched | 0.545 J/cm | 1.02 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 119 °C | 247 °F | ASTM D648 |
Users viewing this material also viewed the following:
- Northstar Polymers PBA-055 Polyether Curing Agent
- SABIC Innovative Plastics Lexan® SLX1432 PC Copolymer (Asia Pacific)
- Techmer ES Luriblend® PC GF20 TL10 BK 20% Glass Filled
- Williams Advanced Alloys Wambraze™ WB1240 Solder
- ExxonMobil Exxsol™ D220/240 Dearomatized Fluid
- Akzo Nobel Expancel® 092 MB 120 Masterbatch with unexpanded microspheres
- BASF Ultramid® TG7S BK-102 35% Glass Filled PA6 (Dry)
Copyright © lookpolymers.com All Rights Reserved