Aardvark Polymers AARTELÂ® 850IM Rotational Molding Resin

Category	Polymer , Thermoplastic , Acetal (POM)
Manufacturer	Gehrig & Associates
Trade Name	AARTEL®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Aardvark Polymers AARTELÂ® 850IM Rotational Molding Resin.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Aartel 850 IM is a moderately toughened impact modified acetal copolymer which exhibits ductility in bending and impact loading. The ductile, rather than brittle, failure mode gives designers more freedom in many applications.Information provided by Gehrig & Associates

Physical Properties	Metric	English	Comments
Density	1.38 g/cc	0.0499 lb/inÂ³	ISO 1183
Linear Mold Shrinkage	0.016 cm/cm	0.016 in/in	ISO 294-4
Linear Mold Shrinkage, Transverse	0.018 cm/cm	0.018 in/in	ISO 294-4
Melt Flow	11.73 g/10 min @Load 2.16 kg, Temperature 190 Â°C	11.73 g/10 min @Load 4.76 lb, Temperature 374 Â°F	ISO 1183

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	55.0 MPa	7980 psi	(50mm/min); ISO 527-2/1A
Elongation at Yield	11 %	11 %	(50mm/min); ISO 527-2/1A
Tensile Modulus	2.15 GPa	312 ksi	(1mm/min); ISO 527-2/1A
Flexural Modulus	1.97 GPa	286 ksi	ISO 178
Izod Impact, Notched (ISO)	8.60 kJ/mÂ² @Temperature 23.0 Â°C	4.09 ft-lb/inÂ² @Temperature 73.4 Â°F	ISO 180/1A
Charpy Impact Unnotched	16.0 J/cmÂ² @Temperature -30.0 Â°C	76.1 ft-lb/inÂ² @Temperature -22.0 Â°F	ISO 179/1e
Charpy Impact, Notched	0.700 J/cmÂ² @Temperature -30.0 Â°C	3.33 ft-lb/inÂ² @Temperature -22.0 Â°F	ISO 179/1e
	1.05 J/cmÂ² @Temperature 23.0 Â°C	5.00 ft-lb/inÂ² @Temperature 73.4 Â°F	ISO 179/1e

Thermal Properties	Metric	English	Comments
Melting Point	165 Â°C	329 Â°F	(10Â°C/min); ISO 11357-1,2,3
Deflection Temperature at 0.46 MPa (66 psi)	161 Â°C	322 Â°F	ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)	84.0 Â°C	183 Â°F	ISO 75-1/-2