Aardvark Polymers AARTEL® 1000 Rotational Molding Resin

Category Polymer , Thermoplastic , Acetal (POM)
Manufacturer Gehrig & Associates
Trade Name AARTEL®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Aardvark Polymers AARTEL® 1000 Rotational Molding Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Aartel 1000 is our premium grade of toughened impact modified acetal copolymer. Aartel 1000 is formulated with high impact properties combined with extended mechanical properties and elevated resistance to aggressive chemicals, fuels, and hydrocarbons.Information provided by Gehrig & Associates
Physical Properties Metric English Comments
Density 1.35 g/cc
0.0488 lb/in³
ISO 1183
Linear Mold Shrinkage 0.016 cm/cm
0.016 in/in
ISO 294-4
Linear Mold Shrinkage, Transverse 0.017 cm/cm
0.017 in/in
ISO 294-4
Melt Flow 2.97 g/10 min

@Load 2.16 kg,
Temperature 190 °C
2.97 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ISO 1183
Mechanical Properties Metric English Comments
Tensile Strength, Yield 45.0 MPa
6530 psi
(50mm/min); ISO 527-2/1A
Elongation at Yield 14 %
14 %
(50mm/min); ISO 527-2/1A
Tensile Modulus 1.75 GPa
254 ksi
(1mm/min); ISO 527-2/1A
Flexural Modulus 1.62 GPa
235 ksi
ISO 178
Izod Impact, Notched (ISO) 15.0 kJ/m²

@Temperature 23.0 °C
7.14 ft-lb/in²

@Temperature 73.4 °F
ISO 180/1A
Charpy Impact, Notched 1.30 J/cm²

@Temperature -30.0 °C
6.19 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1e
1.60 J/cm²

@Temperature 23.0 °C
7.61 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1e
Thermal Properties Metric English Comments
Melting Point 164 °C
327 °F
(10°C/min); ISO 11357-1,2,3
Deflection Temperature at 0.46 MPa (66 psi) 137 °C
279 °F
ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 69.0 °C
156 °F
ISO 75-1/-2