ATI Wah Chang 425™ Titanium Alloy, Hot Rolled & Annealed Plate, Solution Treated Annealed

Category Metal , Nonferrous Metal , Titanium Alloy
Manufacturer ATI Wah Chang
Trade Name 425™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ATI Wah Chang 425™ Titanium Alloy, Hot Rolled & Annealed Plate, Solution Treated Annealed.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
ATI 425™ titanium is an innovative high strength alloy that has strength comparable to Ti-6-4, yet has the advantage that it can be cold worked. Originally developed for armor plate for ballistic protection, it was observed during processing to have exceptional hot workability. ATI 425™ titanium is an alpha-beta alloy that utilizes iron in place of some higher-cost vanadium as a beta stabilizer. Information provided by ATI Wah Chang
Physical Properties Metric English Comments
Density 4.48 g/cc
0.162 lb/in³
Mechanical Properties Metric English Comments
Hardness, Rockwell C 32 - 36
32 - 36
Tensile Strength, Ultimate 1140 MPa
166000 psi
Long.
1180 MPa
171000 psi
Trans.
Tensile Strength, Yield 1020 MPa
148000 psi
Long.
1070 MPa
155000 psi
Trans.
Elongation at Break 12 %
12 %
Long.
12 %
12 %
Trans.
Thermal Properties Metric English Comments
Melting Point 1600 - 1650 °C
2910 - 3000 °F
Solidus 1600 °C
2910 °F
Liquidus 1650 °C
3000 °F
Beta Transus 957 - 971 °C
1750 - 1780 °F
Component Elements Properties Metric English Comments
Aluminum, Al 4.0 %
4.0 %
Iron, Fe 1.5 %
1.5 %
O2 0.25 %
0.25 %
Titanium, Ti 91.75 %
91.75 %
Vanadium, V 2.5 %
2.5 %
Electrical Properties Metric English Comments
Electrical Resistivity 0.000154 ohm-cm
0.000154 ohm-cm