- ATI Allvac® Nickelvac® N-90 Nickel Superalloy, Heat Treatment: 1066°C (1950°F) + Age
ATI Allvac® Nickelvac® N-90 Nickel Superalloy, Heat Treatment: 1066°C (1950°F) + Age
| Category | Metal , Nonferrous Metal , Nickel Alloy , Superalloy |
| Manufacturer | ATI Allvac |
| Trade Name | Nickelvac® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | ATI Allvac® Nickelvac® N-90 Nickel Superalloy, Heat Treatment: 1066°C (1950°F) + Age.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by Allvac.Applications: Turbine blades and other jet engine components. Valves for internal combustion engines.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 8.11 g/cc | 0.293 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Brinell | 278 | 278 | Estimated from Rockwell C value for Brinell test with 3000 kg load/10 mm diameter ball |
| Hardness, Knoop | 301 | 301 | Estimated from Rockwell C value. |
| Hardness, Rockwell C | 28 | 28 | |
| Hardness, Vickers | 292 | 292 | Estimated from Rockwell C value. |
| Tensile Strength, Ultimate | 1207 MPa | 175100 psi | |
| Tensile Strength, Yield | 517 MPa @Strain 0.200 % |
75000 psi @Strain 0.200 % |
|
| Elongation at Break | 30 % | 30 % | |
| Reduction of Area | 35 % | 35 % |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Aluminum, Al | 1.4 % | 1.4 % | |
| Carbon, C | 0.065 % | 0.065 % | |
| Chromium, Cr | 19.5 % | 19.5 % | |
| Cobalt, Co | 18 % | 18 % | |
| Iron, Fe | 0.30 % | 0.30 % | |
| Nickel, Ni | 58 % | 58 % | as balance |
| Titanium, Ti | 2.4 % | 2.4 % |
Users viewing this material also viewed the following:
- Pyrotek ISOMAG® 70 Structural Insulation
- Nilit FRIANYL B63 HH Nylon 6 for injection molding
- Overview of materials for Polycarbonate/PET Polyester Blend, Glass Reinforced
- LG Chemical LUPOL TE-5108 Thermoplastic Elastomer Alloy, 10% Polymer Alloy, High Flow
- Tra-Con Tra-Bond 2116 Low Vapor Pressure Epoxy Staking Compound
- A. Schulman POLYBLAK™ 4479-01 Black Color Concentrate, 50% Carbon Black Based In LLDPE
- Arlon 51808R011 0.011" (0.279 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
- A. Schulman PP 3476 Polypropylene Homopolymer Polypropylene
- Adell AH-18 Nylon 66, 40% Mineral Filled
Copyright © lookpolymers.com All Rights Reserved