ATI Allvac® Nickelvac® H-46 Specialty Steel, Heat Treatment: 1149°C (2100°F) Anneal
| Category | Metal , Ferrous Metal , Stainless Steel |
| Manufacturer | ATI Allvac |
| Trade Name | Nickelvac® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | ATI Allvac® Nickelvac® H-46 Specialty Steel, Heat Treatment: 1149°C (2100°F) Anneal.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by Allvac.Applications: Structural components for land-based turbine engines. Rings and structurals in jet engines.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 7.75 g/cc | 0.280 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Brinell | 304 | 304 | Estimated from Rockwell C value for Brinell test with 3000 kg load/10 mm diameter ball |
| Hardness, Knoop | 330 | 330 | Estimated from Rockwell C value. |
| Hardness, Rockwell C | 32 | 32 | |
| Hardness, Vickers | 318 | 318 | Estimated from Rockwell C value. |
| Tensile Strength, Ultimate | 690 MPa | 100000 psi | |
| Tensile Strength, Yield | 621 MPa @Strain 0.200 % |
90100 psi @Strain 0.200 % |
|
| Elongation at Break | 18 % | 18 % | |
| Reduction of Area | 50 % | 50 % |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Carbon, C | 0.16 % | 0.16 % | |
| Chromium, Cr | 11 % | 11 % | |
| Copper, Cu | 0.20 % | 0.20 % | |
| Iron, Fe | 86 % | 86 % | as balance |
| Manganese, Mn | 0.65 % | 0.65 % | |
| Molybdenum, Mo | 0.75 % | 0.75 % | |
| Nickel, Ni | 0.60 % | 0.60 % | |
| Niobium, Nb (Columbium, Cb) | <= 0.35 % | <= 0.35 % | |
| Nitrogen, N | 0.040 % | 0.040 % | |
| Phosphorous, P | 0.010 % | 0.010 % | |
| Silicon, Si | 0.45 % | 0.45 % | |
| Sulfur, S | 0.0050 % | 0.0050 % | |
| Tantalum, Ta | <= 0.35 % | <= 0.35 % | |
| Vanadium, V | 0.25 % | 0.25 % |