ATI Allegheny Ludlum Type 332 Stainless Steel, UNS N08800

Category Metal , Ferrous Metal , Stainless Steel , T 300 Series Stainless Steel
Manufacturer ATI Allegheny Ludlum
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ATI Allegheny Ludlum Type 332 Stainless Steel, UNS N08800.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Type 332 is a nickel and chromium austenitic stainless steel designed to resist oxidation and carburization at elevated temperatures. The nickel content, 32%, makes the alloy highly resistant both to chloride stress corrosion cracking and to embrittlement from precipitation to sigma phase. The general corrosion resistance is excellent. In the solution annealed condition, Type 332 has superior creep and stress rupture properties. Type 332 has been approved as a material of construction under ASME Boiler and Pressure Vessel Code, Section I - Power Boilers, Section III - Nuclear Vessels, Section VIII - Unfired Pressure Vessels.Information provided by Allegheny Ludlum
Physical Properties Metric English Comments
Density 8.027 g/cc
0.2900 lb/in³
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 600 MPa
87000 psi
Typical; after 1800°F Anneal
Tensile Strength, Yield 294 MPa

@Strain 0.200 %
42600 psi

@Strain 0.200 %
Typical; after 1800°F Anneal
Elongation at Break 44 %
44 %
Typical; after 1800°F Anneal
Reduction of Area 67 %
67 %
Typical; after 1800°F Anneal
Modulus of Elasticity 196 GPa
28400 ksi
typical of UNS N08800
Poissons Ratio 0.34
0.34
typical of UNS N08800
Shear Modulus 73.0 GPa
10600 ksi
typical of UNS N08800
Thermal Properties Metric English Comments
CTE, linear 14.2 µm/m-°C

@Temperature 20.0 - 90.0 °C
7.89 µin/in-°F

@Temperature 68.0 - 194 °F
16.0 µm/m-°C

@Temperature 20.0 - 250 °C
8.89 µin/in-°F

@Temperature 68.0 - 482 °F
16.7 µm/m-°C

@Temperature 20.0 - 500 °C
9.28 µin/in-°F

@Temperature 68.0 - 932 °F
Specific Heat Capacity 0.500 J/g-°C
0.120 BTU/lb-°F
Thermal Conductivity 11.6 W/m-K
80.5 BTU-in/hr-ft²-°F
Melting Point 1357 - 1385 °C
2475 - 2525 °F
Solidus 1357 °C
2475 °F
Liquidus 1385 °C
2525 °F
Component Elements Properties Metric English Comments
Aluminum, Al 0.30 %
0.30 %
Carbon, C 0.030 %
0.030 %
Chromium, Cr 20.5 %
20.5 %
Copper, Cu 0.20 %
0.20 %
Iron, Fe 46 %
46 %
as balance
Manganese, Mn 1.0 %
1.0 %
Nickel, Ni 31 %
31 %
Phosphorous, P 0.020 %
0.020 %
Silicon, Si 0.40 %
0.40 %
Sulfur, S 0.010 %
0.010 %
Titanium, Ti 0.30 %
0.30 %
Electrical Properties Metric English Comments
Electrical Resistivity 0.0000990 ohm-cm
0.0000990 ohm-cm
Magnetic Permeability 1.0092
1.0092
at 200 Oe
Curie Temperature -115 °C
-175 °F