ATI Allegheny Ludlum Martensitic Stainless Steel Type 410, Hardened + 538°C Temper

Category Metal , Ferrous Metal , Stainless Steel , T 400 Series Stainless Steel
Manufacturer ATI Allegheny Ludlum
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ATI Allegheny Ludlum Martensitic Stainless Steel Type 410, Hardened + 538°C Temper.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Allegheny Ludlum Type 410 is a hardenable straight-chromium stainless steel which combines superior wear resistance of high carbon alloys with the excellent corrosion resistance of chromium stainless steel. Oil quenching this alloy from temperatures between 1800°F and 1950°F produces the high strength and/or wear resistance as well as corrosion resistance.A major use for this grade of heat treatable stainless steels is in cutlery. When blanking cutlery parts from annealed raw material stock, Type 410 will usually exhibit hardness, yield strength, and tensile strength that are low enough for fine blanking purposes.UTS, TYS, and hardness values below obtained after austenitizing at 1800-1950°F (982-1066°C) followed by an oil quench and two hour temper as above.Information provided by Allegheny Ludlum Corporation.
Physical Properties Metric English Comments
Density 7.65 g/cc
0.276 lb/in³
Mechanical Properties Metric English Comments
Hardness, Rockwell C 35
35
Tensile Strength, Ultimate 1063 MPa
154200 psi
Typical
Tensile Strength, Yield 882 MPa

@Strain 0.200 %
128000 psi

@Strain 0.200 %
typical
Modulus of Elasticity 200 GPa
29000 ksi
Thermal Properties Metric English Comments
CTE, linear 10.5 µm/m-°C

@Temperature 20.0 - 200 °C
5.83 µin/in-°F

@Temperature 68.0 - 392 °F
11.6 µm/m-°C

@Temperature 20.0 - 600 °C
6.44 µin/in-°F

@Temperature 68.0 - 1110 °F
Thermal Conductivity 24.899 W/m-K

@Temperature 100 °C
172.80 BTU-in/hr-ft²-°F

@Temperature 212 °F
Melting Point 1482 - 1532 °C
2700 - 2790 °F
Solidus 1482 °C
2700 °F
Liquidus 1532 °C
2790 °F
Component Elements Properties Metric English Comments
Carbon, C <= 0.15 %
<= 0.15 %
Chromium, Cr 11.5 - 13.5 %
11.5 - 13.5 %
Iron, Fe 86 %
86 %
as balance
Manganese, Mn <= 1.0 %
<= 1.0 %
Nickel, Ni <= 0.50 %
<= 0.50 %
Phosphorous, P <= 0.040 %
<= 0.040 %
Silicon, Si <= 1.0 %
<= 1.0 %
Sulfur, S <= 0.030 %
<= 0.030 %
Electrical Properties Metric English Comments
Electrical Resistivity 0.0000560 ohm-cm
0.0000560 ohm-cm