ATI Allegheny Ludlum AL 2003™ Duplex Stainless Steel
| Category | Metal , Ferrous Metal , Duplex , Stainless Steel , T S30000 Series Stainless Steel |
| Manufacturer | ATI Allegheny Ludlum |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | ATI Allegheny Ludlum AL 2003™ Duplex Stainless Steel.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Characteristics: superior stress corrosion cracking resistance to Types 316 and 317, yield strength double that of conventional austenitic stainless steel, good corrosion resistance, good chloride stress corrosion cracking resistance. Applications:DesalinationBridge Decking Oil and GasHome AppliancesHeat Exchangers Pressure Vessels Pulp and Paper Tanks Architectural Structures Water Heaters Power Generation Reinforcing Bar Chemical Processing Information provided by Allegheny Ludlum
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 7.723 g/cc | 0.2790 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell C | 20 | 20 | |
| Tensile Strength, Ultimate | 725 MPa | 105000 psi | |
| 745 MPa | 108000 psi | 0% cold reduction | |
| 917 MPa | 133000 psi | 9.4% cold reduction | |
| 1165 MPa | 169000 psi | 27.6% cold reduction | |
| 1620 MPa | 235000 psi | 67.3% cold reduction | |
| 586 MPa @Temperature 260 °C |
85000 psi @Temperature 500 °F |
||
| 600 MPa @Temperature 204 °C |
87000 psi @Temperature 399 °F |
||
| 607 MPa @Temperature 149 °C |
88000 psi @Temperature 300 °F |
||
| 655 MPa @Temperature 93.0 °C |
95000 psi @Temperature 199 °F |
||
| Tensile Strength, Yield | 545 MPa | 79000 psi | 0% cold reduction |
| 827 MPa | 120000 psi | 9.4% cold reduction | |
| 1020 MPa | 148000 psi | 27.6% cold reduction | |
| 1476 MPa | 214100 psi | 67.3% cold reduction | |
| 386 MPa @Temperature 260 °C |
56000 psi @Temperature 500 °F |
||
| 386 MPa @Temperature 204 °C |
56000 psi @Temperature 399 °F |
||
| 427 MPa @Temperature 149 °C |
61900 psi @Temperature 300 °F |
||
| 455 MPa @Temperature 93.0 °C |
66000 psi @Temperature 199 °F |
||
| 515 MPa @Strain 0.200 % |
74700 psi @Strain 0.200 % |
||
| Elongation at Break | 1.0 % | 1.0 % | 67.3% cold reduction |
| 10 % | 10 % | 27.6% cold reduction | |
| 15 % | 15 % | 9.4% cold reduction | |
| 34 % | 34 % | 0% cold reduction | |
| 40 % | 40 % | in 2" | |
| 22 % @Temperature 260 °C |
22 % @Temperature 500 °F |
||
| 26 % @Temperature 204 °C |
26 % @Temperature 399 °F |
||
| 27 % @Temperature 149 °C |
27 % @Temperature 300 °F |
||
| 32 % @Temperature 93.0 °C |
32 % @Temperature 199 °F |
||
| Modulus of Elasticity | 190 GPa | 27600 ksi |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 13.0 µm/m-°C @Temperature 23.0 - 100 °C |
7.22 µin/in-°F @Temperature 73.4 - 212 °F |
|
| Specific Heat Capacity | 0.510 J/g-°C @Temperature 23.0 - 100 °C |
0.122 BTU/lb-°F @Temperature 73.4 - 212 °F |
|
| Thermal Conductivity | 17.0 W/m-K @Temperature 23.0 - 100 °C |
118 BTU-in/hr-ft²-°F @Temperature 73.4 - 212 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Carbon, C | <= 0.030 % | <= 0.030 % | |
| Chromium, Cr | 19.5 - 22.5 % | 19.5 - 22.5 % | |
| Iron, Fe | >= 68.22 % | >= 68.22 % | As Remainder |
| Manganese, Mn | <= 2.0 % | <= 2.0 % | |
| Molybdenum, Mo | 1.5 - 2.0 % | 1.5 - 2.0 % | |
| Nickel, Ni | 3.0 - 4.0 % | 3.0 - 4.0 % | |
| Nitrogen, N | 0.14 - 0.20 % | 0.14 - 0.20 % | |
| Phosphorous, P | <= 0.030 % | <= 0.030 % | |
| Silicon, Si | <= 1.0 % | <= 1.0 % | |
| Sulfur, S | <= 0.020 % | <= 0.020 % |