API Megol AM DP2217/90PBT SEBS Adhesion Modified Overmolding for Polyesters

Category Polymer , Thermoplastic , Elastomer, TPE , Styrenic TPE
Manufacturer A.P.I. SpA
Trade Name Megol AM
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF API Megol AM DP2217/90PBT SEBS Adhesion Modified Overmolding for Polyesters.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Over-molding allows for the creation of composite finished products in a single phase, removing the need for successive gluing or mechanical fixing steps. This also reduces environmental impact as there are no VOC emissions from adhesives and, as the components are not made from a range of incompatible materials, they are more easily recycled at the end of their useful life. The over-molding process can be used in highly technical applications such as components for the automotive industry, shells and casings for power tools, parts for domestic appliances, and seals which can be molded directly onto the frame.Information provided by A.P.I. SpA
Physical Properties Metric English Comments
Density 1.05 g/cc
0.0379 lb/in³
ASTM D 792
Mechanical Properties Metric English Comments
Hardness, Shore A 90

@Time 15.0 sec
90

@Time 0.00417 hour
ASTM D 2240
Tensile Strength 7.00 MPa
1020 psi
ASTM D 638
Elongation at Break 450 %
450 %
ASTM D 638
100% Modulus 0.00400 GPa
0.580 ksi
ASTM D 638
300% Modulus 0.00650 GPa
0.943 ksi
ASTM D 638
Tear Strength 50.0 kN/m
285 pli
ASTM D 624
Compression Set 45 %

@Temperature 23.0 °C,
Time 259000 sec
45 %

@Temperature 73.4 °F,
Time 72.0 hour
ASTM D 395
75 %

@Temperature 70.0 °C,
Time 86400 sec
75 %

@Temperature 158 °F,
Time 24.0 hour
ASTM D 395
90 %

@Temperature 100 °C,
Time 86400 sec
90 %

@Temperature 212 °F,
Time 24.0 hour
ASTM D 395
Descriptive Properties Value Comments
Compatibility PBT
PC
PET
Food contact On Request
Hygroscopicity Slightly
Main Features Easy Processability
Ozone Aging Resistance Excellent
72h, 40°C, 200 ppcm, Tension = 20%
Processing Injection Molding
Weathering Good