AMT AM-Lite® Die Casting Magnesium Alloy
| Category | Metal , Nonferrous Metal , Magnesium Alloy |
| Manufacturer | Advanced Magnesium Technologies (AMT) |
| Trade Name | AM-Lite® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | AMT AM-Lite® Die Casting Magnesium Alloy.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
AM-lite is a high surface finish die casting alloy suitable for applications that currently utilize zinc, aluminum or magnesium (alloy AZ91D) die castings, or plastic injection moldings. AM-lite has better die casting properties than existing magnesium alloys, plus an improved as-cast surface finish that is suitable for decorative surface finishing operations. A special electroplating process has been developed for AM-Lite to take advantage of these properties.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 2.02 g/cc | 0.0730 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Brinell | 76 - 80 | 76 - 80 | |
| Hardness, Vickers | 85 - 90 | 85 - 90 | 300 g |
| Tensile Strength, Ultimate | 230 - 250 MPa | 33400 - 36300 psi | |
| Tensile Strength, Yield | 160 - 170 MPa @Strain 0.200 % |
23200 - 24700 psi @Strain 0.200 % |
|
| Elongation at Break | 3.0 - 4.0 % | 3.0 - 4.0 % | |
| Creep Strength | 35.0 MPa @Temperature 150 °C, Time 720000 sec |
5080 psi @Temperature 302 °F, Time 200 hour |
0.2% strain |
| 60.0 MPa @Temperature 150 °C, Time 720000 sec |
8700 psi @Temperature 302 °F, Time 200 hour |
0.5% strain | |
| Modulus of Elasticity | 45.3 GPa | 6570 ksi | |
| Compressive Yield Strength | 150 MPa | 21800 psi | 0.2% proof |
| Compressive Strength | 446 MPa | 64700 psi | |
| Poissons Ratio | 0.35 | 0.35 | |
| Fatigue Strength | 85.0 MPa @# of Cycles 5.00e+7 |
12300 psi @# of Cycles 5.00e+7 |
R.R.Moore |
| 181 MPa @# of Cycles 1.00e+6 |
26300 psi @# of Cycles 1.00e+6 |
3 point bend; R=0.1 | |
| Shear Modulus | 16.8 GPa | 2440 ksi | |
| Charpy Impact | 3.30 J | 2.43 ft-lb | 10x10 mm, Unnotched |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Heat of Fusion | 340 J/g | 146 BTU/lb | |
| CTE, linear | 24.9 µm/m-°C | 13.8 µin/in-°F | |
| Specific Heat Capacity | 0.950 J/g-°C | 0.227 BTU/lb-°F | |
| Thermal Conductivity | 83.0 W/m-K | 576 BTU-in/hr-ft²-°F | |
| Melting Point | 330 - 585 °C | 626 - 1090 °F | |
| Solidus | 330 °C | 626 °F | |
| Liquidus | 585 °C | 1090 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 0.000105 - 0.000110 ohm-cm | 0.000105 - 0.000110 ohm-cm |