ALM PA-840-GSL Filled Nylon 12 Prototyping Polymer

Category Polymer , Rapid Prototyping Polymer , Thermoplastic , Nylon , Nylon 12
Manufacturer ALM Advanced Laser Materials
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ALM PA-840-GSL Filled Nylon 12 Prototyping Polymer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Engineered for excellent mechanical properties, part definition and surface finish.Stabilized against thermal degradation resulting in little or no scrap material, with typical virgin refresh rates from 15 to 25%.Good temperature control is required to process this material.Information provided by Advanced Laser Materials (ALM).
Physical Properties Metric English Comments
Bulk Density 0.420 g/cc
0.0152 lb/in³
ASTM D1895
Density 0.870 g/cc
0.0314 lb/in³
Sintered; ASTM D792
Particle Size 50 µm
50 µm
D50
38 - 78 µm
38 - 78 µm
D10-D90
Melt Flow 13 g/10 min

@Load 5.00 kg,
Temperature 235 °C
13 g/10 min

@Load 11.0 lb,
Temperature 455 °F
3 min; ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 37.0 MPa
5370 psi
Z; ASTM D638
48.0 MPa
6960 psi
XY; ASTM D638
Elongation at Break 3.0 %
3.0 %
Z; ASTM D638
4.0 %
4.0 %
XY; ASTM D638
Tensile Modulus 2.137 GPa
309.9 ksi
Z; ASTM D638
3.378 GPa
489.9 ksi
XY; ASTM D638
Thermal Properties Metric English Comments
Melting Point 200 °C
392 °F
ASTM D3418