ALM PA 606-FR Filled Nylon 12 Prototyping Polymer

Category	Polymer , Rapid Prototyping Polymer , Thermoplastic , Nylon , Nylon 12
Manufacturer	ALM Advanced Laser Materials
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	ALM PA 606-FR Filled Nylon 12 Prototyping Polymer.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Only commercially available fire retardant nylon 12 material, which meets FAR 25.853 60 second burn specification.The parts produced from PA 606-FR have a much smoother surface finish and sharper feature detail when compared to FR-106.The PA 606-FR will have both mechanical and physical property characteristics similar to PA 650. Information provided by Advanced Laser Materials (ALM).

Physical Properties	Metric	English	Comments
Bulk Density	0.460 g/cc	0.0166 lb/in³	ASTM D1895
Density	1.02 g/cc	0.0368 lb/in³	ASTM D792
Particle Size	55 µm	55 µm	D50
	30 - 100 µm	30 - 100 µm	D10-D90
Melt Flow	50 g/10 min @Load 5.00 kg, Temperature 235 °C	50 g/10 min @Load 11.0 lb, Temperature 455 °F	3 min; ASTM D1238

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	48.0 MPa	6960 psi	XY; ASTM D638
Elongation at Break	24 %	24 %	XY; ASTM D638
Tensile Modulus	1.70 GPa	247 ksi	XY; ASTM D638
Flexural Modulus	1.50 GPa	218 ksi	XY; ASTM D790
Izod Impact, Notched	2.20 J/cm	4.12 ft-lb/in	ASTM D256
Izod Impact, Unnotched	4.40 J/cm	8.24 ft-lb/in	ASTM D256

Thermal Properties	Metric	English	Comments
Melting Point	181 °C	358 °F	ASTM D3418
Deflection Temperature at 0.46 MPa (66 psi)	177 °C	351 °F	ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	86.0 °C	187 °F	ASTM D648

Electrical Properties	Metric	English	Comments
Volume Resistivity	3.10e+14 ohm-cm	3.10e+14 ohm-cm	50% RH, 500V; ASTM D257
Surface Resistance	3.00e+14 ohm	3.00e+14 ohm	50% RH, 500V; ASTM D257
Dielectric Constant	2.9	2.9	50% RH, 500V; ASTM D150