- AK Steel 17-4 PH® Precipitation Hardening Stainless Steel, Condition H 900
AK Steel 17-4 PH® Precipitation Hardening Stainless Steel, Condition H 900
| Category | Metal , Ferrous Metal , Martensitic , Stainless Steel , Precipitation Hardening Stainless |
| Manufacturer | AK Steel |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | AK Steel 17-4 PH® Precipitation Hardening Stainless Steel, Condition H 900.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
AK Steel 17-4 PH® provides an outstanding combination of high strength, good corrosion resistance, good mechanical properties at temperatures up to 600°F (316°C), and good toughness in both base metal and welds. Short-time, low-temperature heat treatments minimize distortion and scaling. This alloy is widely used in the aerospace, chemical, petrochemical, food processing, paper and general metalworking industries. The material supplied from the mill is in Condition A. After fabrication eight standard heat treatments have been developed to provide a wide range of properties.Information provided by AK Steel
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 7.80 g/cc | 0.282 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell C | 45 | 45 | |
| Tensile Strength, Ultimate | 1448 MPa | 210000 psi | |
| Tensile Strength, Yield | 1379 MPa @Strain 0.200 % |
200000 psi @Strain 0.200 % |
|
| Elongation at Break | 7.0 % | 7.0 % | in 2 inches |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 10.8 µm/m-°C @Temperature 21.0 - 93.0 °C |
6.00 µin/in-°F @Temperature 69.8 - 199 °F |
|
| 11.7 µm/m-°C @Temperature <=427 °C |
6.50 µin/in-°F @Temperature <=801 °F |
||
| Specific Heat Capacity | 0.460 J/g-°C | 0.110 BTU/lb-°F | |
| Thermal Conductivity | 17.9 W/m-K @Temperature 149 °C |
124 BTU-in/hr-ft²-°F @Temperature 300 °F |
|
| 22.6 W/m-K @Temperature 482 °C |
157 BTU-in/hr-ft²-°F @Temperature 900 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Carbon, C | <= 0.070 % | <= 0.070 % | |
| Chromium, Cr | 15 - 17.5 % | 15 - 17.5 % | |
| Copper, Cu | 3.0 - 5.0 % | 3.0 - 5.0 % | |
| Iron, Fe | 69.91 - 78.85 % | 69.91 - 78.85 % | As Remainder |
| Manganese, Mn | <= 1.0 % | <= 1.0 % | |
| Nb + Ta | 0.15 - 0.45 % | 0.15 - 0.45 % | |
| Nickel, Ni | 3.0 - 5.0 % | 3.0 - 5.0 % | |
| Phosphorous, P | <= 0.040 % | <= 0.040 % | |
| Silicon, Si | <= 1.0 % | <= 1.0 % | |
| Sulfur, S | <= 0.030 % | <= 0.030 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 0.0000770 ohm-cm | 0.0000770 ohm-cm |