- AK Steel 17-4 PH® Precipitation Hardening Stainless Steel, Condition H 1150
AK Steel 17-4 PH® Precipitation Hardening Stainless Steel, Condition H 1150
| Category | Metal , Ferrous Metal , Martensitic , Stainless Steel , Precipitation Hardening Stainless |
| Manufacturer | AK Steel |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | AK Steel 17-4 PH® Precipitation Hardening Stainless Steel, Condition H 1150.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
AK Steel 17-4 PH® provides an outstanding combination of high strength, good corrosion resistance, good mechanical properties at temperatures up to 600°F (316°C), and good toughness in both base metal and welds. Short-time, low-temperature heat treatments minimize distortion and scaling. This alloy is widely used in the aerospace, chemical, petrochemical, food processing, paper and general metalworking industries. The material supplied from the mill is in Condition A. After fabrication eight standard heat treatments have been developed to provide a wide range of properties.Information provided by AK Steel
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 7.82 g/cc | 0.283 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell C | 35 | 35 | |
| Tensile Strength, Ultimate | 1103 MPa | 160000 psi | |
| Tensile Strength, Yield | 1034 MPa @Strain 0.200 % |
150000 psi @Strain 0.200 % |
|
| Elongation at Break | 11 % | 11 % | in 2 inches |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 11.9 µm/m-°C @Temperature 21.0 - 93.0 °C |
6.61 µin/in-°F @Temperature 69.8 - 199 °F |
|
| 13.0 µm/m-°C @Temperature <=427 °C |
7.22 µin/in-°F @Temperature <=801 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Carbon, C | <= 0.070 % | <= 0.070 % | |
| Chromium, Cr | 15 - 17.5 % | 15 - 17.5 % | |
| Copper, Cu | 3.0 - 5.0 % | 3.0 - 5.0 % | |
| Iron, Fe | 69.91 - 78.85 % | 69.91 - 78.85 % | As Remainder |
| Manganese, Mn | <= 1.0 % | <= 1.0 % | |
| Nb + Ta | 0.15 - 0.45 % | 0.15 - 0.45 % | |
| Nickel, Ni | 3.0 - 5.0 % | 3.0 - 5.0 % | |
| Phosphorous, P | <= 0.040 % | <= 0.040 % | |
| Silicon, Si | <= 1.0 % | <= 1.0 % | |
| Sulfur, S | <= 0.030 % | <= 0.030 % |