AGY ADVANTEX® Generic Glass Fiber

Category Ceramic , Glass , Glass Fiber , Oxide , Silicon Oxide , Other Engineering Material , Composite Fibers
Manufacturer AGY Holding Corp.
Trade Name ADVANTEX®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF AGY ADVANTEX® Generic Glass Fiber.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
OC/AGY E-CR glass. Various silanes and starch oil are used as binders. Acid resistant. Lower alkali resistance than VeTron® and ZenTron® glass fibers.Information provided by AGY Holding Corp.
Physical Properties Metric English Comments
Density 2.624 g/cc
0.09480 lb/in³
Water Absorption 0.00 %
0.00 %
Loss On Ignition 0.50 - 1.5 %
0.50 - 1.5 %
Varies according to size type
Filament Diameter 9.0 - 30 µm
9.0 - 30 µm
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 2450 MPa

@Temperature 371 °C
355000 psi

@Temperature 700 °F
3200 - 3750 MPa

@Temperature 23.0 °C
464000 - 544000 psi

@Temperature 73.4 °F
Elongation at Break 4.5 %
4.5 %
in 50 mm
Modulus of Elasticity 80.0 GPa
11600 ksi
Thermal Properties Metric English Comments
CTE, linear 5.80 µm/m-°C

@Temperature -30.0 - 300 °C
3.22 µin/in-°F

@Temperature -22.0 - 572 °F
average, isotropic
Specific Heat Capacity 0.970 J/g-°C

@Temperature 200 °C
0.232 BTU/lb-°F

@Temperature 392 °F
Melting Point 1171 °C
2140 °F
Liquidus
Liquidus 1171 °C
2140 °F
Maximum Service Temperature, Air 740 °C
1360 °F
Maximum Service Temperature, Inert 740 °C
1360 °F
Transformation Temperature, Tg 750 °C
1380 °F
Softening Point 916 °C
1680 °F
Optical Properties Metric English Comments
Refractive Index 1.56
1.56
Electrical Properties Metric English Comments
Electrical Resistivity 3.84e+14 ohm-cm
3.84e+14 ohm-cm
Dielectric Constant 7.2

@Frequency 1000 Hz
7.2

@Frequency 1000 Hz
7.5

@Frequency 1e+10 Hz
7.5

@Frequency 1e+10 Hz
Dielectric Strength 10.0 kV/mm
254 kV/in
Dissipation Factor 0.0028
0.0028