Material Notes:
High temperature nickel alloy castings. Applications include heat treatment and handling products, furnace products, tubes, power generation, and petrochemical industries.Information provided by AFE Technologies/North American Cronite, Inc.
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 550 MPa
79800 psi
As Cast
Tensile Strength, Yield 280 MPa
40600 psi
As Cast
Elongation at Break 15 %
15 %
As Cast; 5.65 A<sup>0.5</sup>
Rupture Strength 3.60 MPa

@Temperature 1100 °C,
Time 3.60e+7 sec
522 psi

@Temperature 2010 °F,
Time 10000 hour
Stress Rupture
5.70 MPa

@Temperature 1050 °C,
Time 3.60e+7 sec
827 psi

@Temperature 1920 °F,
Time 10000 hour
Stress Rupture
8.50 MPa

@Temperature 1000 °C,
Time 3.60e+7 sec
1230 psi

@Temperature 1830 °F,
Time 10000 hour
Stress Rupture
12.0 MPa

@Temperature 950 °C,
Time 3.60e+7 sec
1740 psi

@Temperature 1740 °F,
Time 10000 hour
Stress Rupture
17.0 MPa

@Temperature 900 °C,
Time 3.60e+7 sec
2470 psi

@Temperature 1650 °F,
Time 10000 hour
Stress Rupture
24.0 MPa

@Temperature 850 °C,
Time 3.60e+7 sec
3480 psi

@Temperature 1560 °F,
Time 10000 hour
Stress Rupture
33.0 MPa

@Temperature 800 °C,
Time 3.60e+7 sec
4790 psi

@Temperature 1470 °F,
Time 10000 hour
Stress Rupture
46.0 MPa

@Temperature 750 °C,
Time 3.60e+7 sec
6670 psi

@Temperature 1380 °F,
Time 10000 hour
Stress Rupture
66.0 MPa

@Temperature 700 °C,
Time 3.60e+7 sec
9570 psi

@Temperature 1290 °F,
Time 10000 hour
Stress Rupture
Component Elements Properties Metric English Comments
Carbon, C 0.40 %
0.40 %
Chromium, Cr 25 %
25 %
Iron, Fe 60.1 %
60.1 %
As Remainder
Manganese, Mn 1.0 %
1.0 %
Nickel, Ni 12 %
12 %
Silicon, Si 1.5 %
1.5 %