ACC EP QS EPI Engineered Polymers Quick Set Epoxy

Category Polymer , Adhesive , Thermoset , Epoxy
Manufacturer Amber Chemical Company
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ACC EP QS EPI Engineered Polymers Quick Set Epoxy.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
EP QS Quick Set Epoxy, “Powered by Reactamine® Technology”, is a two component 100% solids, no VOC, self-leveling modified epoxy. This versatile new generation epoxy displays low blush, fast cure times, and excellent adhesion characteristics. EP QS can be used as a surface tolerant primer or as a final coat, and will cure in a variety of harsh situations including high humidity. EP QS can be applied at temperatures ranging from 40° F to 120° F. This environmentally friendly epoxy displays excellent chemical resistance, water insensitivity, and UV resistance. EP QS will provide a glossy smooth finish when fully cured. Aggregate can be broadcast into this self-leveling material to provide a non-skid surface. EP QS emits virtually no odors and can be applied indoors with minimal disturbance contributed to high VOC levels found in most epoxies and polyurethanes.ApplicationsEP QS adheres well to several substrates including concrete, steel, and wood. Some typical uses include: CHEMICAL RESISTANT SECONDARY CONTAINMENT OFFSHORE PLATFORMS MAINTENANCE FACILITIES PRIMER FOR MOST POLYUREAS/POLYURETHANES USDA AND FDA ACCEPTABLE COATING INDUSTRIAL FLOORING TANK COATINGPart of the Amber Chemical Group. Data provided by manufacturer.
Physical Properties Metric English Comments
Viscosity 100 cP
100 cP
Hardener
1500 cP
1500 cP
Resin
Mechanical Properties Metric English Comments
Hardness, Shore D 70
70
ASTM D2240
Tensile Strength, Yield 61.23 MPa
8881 psi
ASTM D638
Elongation at Break 28 %
28 %
ASTM D638
Flexural Strength 87.370 MPa
12672 psi
ASTM D790
Flexural Modulus 3.34 GPa
485 ksi
ASTM D638
Adhesive Bond Strength 1.72 MPa
250 psi
Wood (no primer), Delamination; ASTM D4541 Elcometer
>= 2.07 MPa
>= 300 psi
Concrete (no primer), Concrete Failure; ASTM D4541 Elcometer
>= 10.3 MPa
>= 1500 psi
Steel (no primer), Substrate Failure; ASTM D4541 Elcometer
Izod Impact, Notched 3.74 J/cm
7.00 ft-lb/in
ASTM D628
Taber Abrasion, mg/1000 Cycles 80
80
CS17 WHEEL, 1kg per 1000 cycles; ASTM D4060
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 63.0 °C
145 °F
ASTM D648
Flash Point >= 93.3 °C
>= 200 °F
ASTM Pensky-Martin
Processing Properties Metric English Comments
Cure Time >= 150 min

@Temperature 75.0 °C
>= 2.50 hour

@Temperature 167 °F
tack free
Gel Time 20.0 min
20.0 min
75°C
Descriptive Properties Value Comments
Color Light Gray, Dark Gray
Resistance to Acetic Acid (100%) Recommended
Resistance to Acetone Recommended
Resistance to Ammonium Hydroxide (50%) Recommended
Resistance to Brake Fluid (310g/l) Recommended
Resistance to Brine-Saturated H2O Recommended
Resistance to Brine-Saturated H<sub>2</sub>O (310g/l)
Resistance to Gasoline Recommended
Resistance to H2O Recommended
Resistance to Hydrochloric Acid (50%) Recommended
Resistance to MEK Recommended
Resistance to Methanol Recommended
Resistance to Muriatic Acid (10%) Recommended
Resistance to NaCl/H2O (10%) Recommended
Resistance to Nitric Acid (20%) Recommended Conditional
Resistance to Potassium Hydroxide (10%) Recommended
Resistance to Potassium Hydroxide (20%) Recommended, Discoloration
Resistance to Sodium Bicarbonate Recommended
Resistance to Sodium Hydroxide (50%) Recommended, Discoloration
Resistance to Sodium Hypochlorite (10%) Recommended
Resistance to Sugar/H2O Recommended
Resistance to Sulfuric Acid (>50%) Recommended
Resistance to Sulfuric Acid (10%) Recommended
Resistance to Toluene Contact EPI
Resistance to Xylene Recommended Conditional