- A. Schulman SCHULAMID® 6 GB30 30% Glass Bead Reinforced Nylon 6
A. Schulman SCHULAMID® 6 GB30 30% Glass Bead Reinforced Nylon 6
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Glass Bead Filled |
| Manufacturer | A. Schulman, Inc. |
| Trade Name | SCHULAMID® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | A. Schulman SCHULAMID® 6 GB30 30% Glass Bead Reinforced Nylon 6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by A. Schulman.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.32 g/cc | 1.32 g/cc | ISO 1183/1 |
| Linear Mold Shrinkage | 0.011 cm/cm @Thickness 3.175 mm |
0.011 in/in @Thickness 0.1250 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 60.0 MPa | 8700 psi | ISO 527 |
| Tensile Strength, Yield | 62.1 MPa | 9000 psi | ISO 527 |
| Flexural Strength | 109 MPa | 15800 psi | ISO 178 |
| Flexural Modulus | 4.395 GPa | 637.4 ksi | ISO 178 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 185 °C | 365 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 73.9 °C | 165 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 270 - 295 °C | 518 - 563 °F | |
| Mold Temperature | 65.6 - 93.3 °C | 150 - 200 °F | |
| Drying Temperature | 79.4 °C | 175 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | Predrying |