A. Schulman POLYFORT™ PP 3701
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | A. Schulman, Inc. |
| Trade Name | POLYFORT™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | A. Schulman POLYFORT™ PP 3701.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by A. Schulman.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.915 g/cc | 0.915 g/cc | ASTM D792 |
| Melt Flow | 15 - 25 g/10 min | 15 - 25 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 18.0 MPa | 2610 psi | ASTM D638 |
| Elongation at Break | 25 % | 25 % | ASTM D638 |
| Flexural Strength | 20.0 MPa | 2900 psi | ASTM D790 |
| Flexural Modulus | 0.700 GPa | 102 ksi | ASTM D790 |
| Izod Impact, Notched | 4.50 J/cm | 8.43 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 68.0 °C | 154 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 44.0 °C | 111 °F | ASTM D648 |
Users viewing this material also viewed the following:
- Precision Polymer Engineering Z75Y Hydrogenated NBR Compound
- Kolon Kocetal® EC701 Modified Grade Acetal Copolymer (discontinued **)
- Magyar Aluminum ALO-Ex32 Alumina
- Materion Beryllium Copper Alloy 165 Rod and Bar; HT (TH04) Temper; over 25.4 to 76 mm (UNS C17000)
- Silberline Dedusted Flake Series DF-3500 Aluminum Flake
- A. Schulman SCHULINK® X XL350 Cross-Linkable, High Density Polyethylene
- Tisan TISLAMID® 66 15% Glass Fiber Reinforced Nylon 66
- Wellman Wellamid® GFT13-66 XE-NBK1 13% Glass Fiber Reinforced, Impact Modified Nylon 66
- A. Schulman POLYBATCH™ White 8350 AP Concentrate Based In LDPE
- ACC MM925 Condensation Cure 2-Part Molding Rubber
Copyright © lookpolymers.com All Rights Reserved