A. Schulman POLYFORT™ FPP 1512E Talc Filled, High Impact Copolymer Polypropylene

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 10% Talc Filler
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF A. Schulman POLYFORT™ FPP 1512E Talc Filled, High Impact Copolymer Polypropylene.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
DescriptionPolyfort® FPP 1512E is a 10% talc-filled, high impact copolymer polypropylene. ApplicationPolyfort® FPP 1512E is suitable for extrusion or blow molding applications. Information provided by A. Schulman.
Physical Properties Metric English Comments
Specific Gravity 0.957 g/cc
0.957 g/cc
ASTM D792
Melt Flow 0.75 g/10 min

@Temperature 230 °C
0.75 g/10 min

@Temperature 446 °F
Condition L; ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 80
80
ASTM D785
Tensile Strength, Yield 26.37 MPa
3825 psi
2 in/min; ASTM D638
Elongation at Break 13 %
13 %
ASTM D638
Flexural Strength 35.54 MPa
5155 psi
ASTM D790
Flexural Modulus 1.68 GPa
244 ksi
ASTM D790
2.20 GPa
319 ksi
1.3 mm/min; ASTM D790
Izod Impact, Notched 2.83 J/cm
5.30 ft-lb/in
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 116 °C
240 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 76.7 °C
170 °F
ASTM D648