A. Schulman ComAlloy Lubrilon® 62S1 Internally Lubricated, Nylon 6/6

Category	Polymer , Thermoplastic , Nylon , Nylon 66
Manufacturer	A. Schulman ComAlloy
Trade Name	Lubrilon®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	A. Schulman ComAlloy Lubrilon® 62S1 Internally Lubricated, Nylon 6/6.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Data provided by the manufacturer, ComAlloy International Company. High performance and excellent lubricity with minimal surface wear.The ComAlloy product line has been integrated into the A Schulman product line.

Physical Properties	Metric	English	Comments
Density	1.13 g/cc	0.0408 lb/in³
Linear Mold Shrinkage	0.0070 cm/cm	0.0070 in/in	ASTM D955

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	118	118	ASTM D785
Tensile Strength, Ultimate	80.0 MPa	11600 psi	ASTM D638
Elongation at Break	17 %	17 %	ASTM D638
Flexural Yield Strength	103 MPa	14900 psi	ASTM D790
Flexural Modulus	3.00 GPa	435 ksi	ASTM D790
Izod Impact, Notched	0.400 J/cm	0.749 ft-lb/in	ASTM D256
Izod Impact, Unnotched	NB	NB	ASTM D256
Coefficient of Friction, Dynamic	0.10	0.10
Coefficient of Friction, Static	0.090	0.090
K (wear) Factor	80.6 x 10^-8 mm³/N-M	40.0 x 10^-10 in³-min/ft-lb-hr	K=W/PVT where W=wear (inches^3); P=applied pressure (psi); V=velocity (fpm); T=time (hours).
Limiting Pressure Velocity	0.280 MPa-m/sec	7990 psi-ft/min	at 0.35 m/s

Thermal Properties	Metric	English	Comments
Melting Point	255 - 275 °C	491 - 527 °F
Deflection Temperature at 0.46 MPa (66 psi)	184 °C	363 °F	ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	68.0 °C	154 °F	ASTM D648