A. Schulman ComAlloy E-16822-1B Internally Lubricated, Carbon Fiber Reinforced Nylon 6/6

Category Polymer , Thermoplastic , Nylon , Nylon 66
Manufacturer A. Schulman ComAlloy
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF A. Schulman ComAlloy E-16822-1B Internally Lubricated, Carbon Fiber Reinforced Nylon 6/6.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Data provided by the manufacturer, ComAlloy International Company. High performance and excellent lubricity with minimal surface wear.The ComAlloy product line has been integrated into the A Schulman product line.
Physical Properties Metric English Comments
Density 1.33 g/cc
0.0480 lb/in³
Linear Mold Shrinkage 0.0020 cm/cm
0.0020 in/in
ASTM D955
Mechanical Properties Metric English Comments
Hardness, Rockwell R 117
117
ASTM D785
Tensile Strength, Ultimate 164 MPa
23800 psi
ASTM D638
Elongation at Break 3.0 %
3.0 %
ASTM D638
Flexural Yield Strength 234 MPa
33900 psi
ASTM D790
Flexural Modulus 14.0 GPa
2030 ksi
ASTM D790
Izod Impact, Notched 0.700 J/cm
1.31 ft-lb/in
ASTM D256
Izod Impact, Unnotched 5.40 J/cm
10.1 ft-lb/in
ASTM D256
Coefficient of Friction, Dynamic 0.17
0.17
Coefficient of Friction, Static 0.20
0.20
K (wear) Factor 15.9 x 10-8 mm³/N-M
7.90 x 10-10 in³-min/ft-lb-hr
K=W/PVT where W=wear (inches^3); P=applied pressure (psi); V=velocity (fpm); T=time (hours).
Limiting Pressure Velocity 3.29 MPa-m/sec
93900 psi-ft/min
at 0.35 m/s
Thermal Properties Metric English Comments
Melting Point 255 - 275 °C
491 - 527 °F
Deflection Temperature at 0.46 MPa (66 psi) 263 °C
505 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 254 °C
489 °F
ASTM D648