A. Schulman ComAlloy E-16769N Internally Lubricated, Glass Fiber Reinforced PPS

Category Polymer , Thermoplastic , Polyphenylene Sulfide (PPS)
Manufacturer A. Schulman ComAlloy
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF A. Schulman ComAlloy E-16769N Internally Lubricated, Glass Fiber Reinforced PPS.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Data provided by the manufacturer, ComAlloy International Company. High performance and excellent lubricity with minimal surface wear.The ComAlloy product line has been integrated into the A Schulman product line.
Physical Properties Metric English Comments
Density 1.69 g/cc
0.0611 lb/in³
Linear Mold Shrinkage 0.0020 cm/cm
0.0020 in/in
ASTM D955
Mechanical Properties Metric English Comments
Hardness, Rockwell R 121
121
ASTM D785
Tensile Strength, Ultimate 124 MPa
18000 psi
ASTM D638
Elongation at Break 2.0 %
2.0 %
ASTM D638
Flexural Yield Strength 165 MPa
23900 psi
ASTM D790
Flexural Modulus 9.00 GPa
1310 ksi
ASTM D790
Izod Impact, Notched 0.600 J/cm
1.12 ft-lb/in
ASTM D256
Izod Impact, Unnotched 5.60 J/cm
10.5 ft-lb/in
ASTM D256
Coefficient of Friction, Dynamic 0.16
0.16
Coefficient of Friction, Static 0.13
0.13
K (wear) Factor 32.2 x 10-8 mm³/N-M
16.0 x 10-10 in³-min/ft-lb-hr
K=W/PVT where W=wear (inches^3); P=applied pressure (psi); V=velocity (fpm); T=time (hours).
Thermal Properties Metric English Comments
Melting Point 280 - 290 °C
536 - 554 °F
Deflection Temperature at 0.46 MPa (66 psi) 279 °C
534 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 255 °C
491 °F
ASTM D648